Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Relative Dichte | 23.0 °C | 1.39 [-] Show Supplier Material materials with Relative Dichte of 1.39 [-] | ASTM D 792 | |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 350 MPa Show Supplier Material materials with Biegefestigkeit of 350 MPa | ISO 178 | 2 mm/min |
Biegemodul | 23.0 °C | 23.3 GPa Show Supplier Material materials with Biegemodul of 23.3 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 1.4 % Show Supplier Material materials with Dehnung of 1.4 % | ISO 527 | break, 5 mm/min |
Druckfestigkeit | 23.0 °C | 234 MPa Show Supplier Material materials with Druckfestigkeit of 234 MPa | SABIC method |
Elastizitätsmodul | 23.0 °C | 27.5 GPa Show Supplier Material materials with Elastizitätsmodul of 27.5 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 80 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 80 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 580 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 580 J/m | ASTM D 4812 | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 7 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 7 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 32 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 32 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 257 MPa Show Supplier Material materials with Zugfestigkeit of 257 MPa | ISO 527 | break, 5 mm/min |
Thermisch
Property | Value | Comment |
---|---|---|
Heat deflection temperature, 1.80 MPa | 198 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 198 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
Wärmeformbeständigkeitstemperatur | 198 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 198 °C |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 10 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 10 g/10min | ASTM D 1238 | 380°C/6.7 kgf | |
Schrumpfung | 23.0 °C | 0.1 % Show Supplier Material materials with Schrumpfung of 0.1 % | ASTM D 955 | 24 hrs |
Schrumpfung, diagonal | 23.0 °C | 0.1 % Show Supplier Material materials with Schrumpfung, diagonal of 0.1 % | ASTM D 955 | 24 hrs |
Technological properties
Property | ||
---|---|---|
Application areas | Water Treatment/Filtration, Respiratory, Surgical Devices | |
Availability | Europe,Asia,Americas | |
Processing methods | Maximum Moisture Content: 0.02% | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |