Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 15 MPa Show Supplier Material materials with Biegefestigkeit of 15 MPa | ISO 178 | break, 2 mm/min |
Biegemodul | 23.0 °C | 2.8 GPa Show Supplier Material materials with Biegemodul of 2.8 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 1.2 % Show Supplier Material materials with Dehnung of 1.2 % | ISO 527 | break, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 2.6 GPa Show Supplier Material materials with Elastizitätsmodul of 2.6 GPa | ISO 527 | 1 mm/min |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 3.5 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 3.5 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 5.5 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 5.5 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 20 MPa Show Supplier Material materials with Zugfestigkeit of 20 MPa | ISO 527 | break, 5 mm/min |
Thermisch
Property | Temperature | Value | Comment |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 100 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 100 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 60 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 60 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.3E-4 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.3E-4 1/K | ISO 11359-2 | 23°C to 60°C |
Wärmeformbeständigkeitstemperatur | 60 - 100 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 60 - 100 °C | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.5E-4 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.5E-4 1/K | ISO 11359-2 | 23°C to 60°C |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 100MHz | 23.0 °C | 13.6 [-] Show Supplier Material materials with Dielectric constant, 100MHz of 13.6 [-] | IEC 60250 | 100 MHz |
Dielectric constant, 1GHz | 23.0 °C | 13.1 [-] Show Supplier Material materials with Dielectric constant, 1GHz of 13.1 [-] | IEC 60250 |
Dielectric constant, 500MHz | 23.0 °C | 13.4 [-] Show Supplier Material materials with Dielectric constant, 500MHz of 13.4 [-] | IEC 60250 |
Dissipation factor, 100MHz | 23.0 °C | 9E-3 [-] Show Supplier Material materials with Dissipation factor, 100MHz of 9E-3 [-] | IEC 60250 | 100 MHz |
Dissipation factor, 1GHz | 23.0 °C | 8E-3 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 8E-3 [-] | IEC 60250 |
Dissipation factor, 500MHz | 23.0 °C | 8E-3 [-] Show Supplier Material materials with Dissipation factor, 500MHz of 8E-3 [-] | IEC 60250 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzvolumenflussrate | 7.5 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 7.5 cm³/10min | ISO 1133 | MVR at 190°C/10.0 kg | |
Schrumpfung | 23.0 °C | 1.5 % Show Supplier Material materials with Schrumpfung of 1.5 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Enclosures | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 80°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |