Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.43 g/cm³ Show Supplier Material materials with Dichte of 1.43 g/cm³ | ASTM D 792 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 207 MPa Show Supplier Material materials with Biegefestigkeit of 207 MPa | ISO 178 |
Biegemodul | 23.0 °C | 7.7 GPa Show Supplier Material materials with Biegemodul of 7.7 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 1.7 % Show Supplier Material materials with Dehnung of 1.7 % | ISO 527 | break, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 7.6 GPa Show Supplier Material materials with Elastizitätsmodul of 7.6 GPa | ISO 527 | 1 mm/min |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 4 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 4 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 30 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 30 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 124 MPa Show Supplier Material materials with Zugfestigkeit of 124 MPa | ISO 527 | break, 5 mm/min |
Technological properties
Property | ||
---|---|---|
Application areas | Gear/Bearing/Slider, Electronic Components, Air Cabin Interiors | |
Availability | Europe,Asia,Americas | |
Processing methods | Rear - Zone 1 Temperature: 370 to 380.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |