Allgemein
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 96 MPa Show Supplier Material materials with Biegefestigkeit of 96 MPa | ASTM D 790 | yld, 1.3 mm/min, 50 mm span |
Biegemodul | 23.0 °C | 2.3 GPa Show Supplier Material materials with Biegemodul of 2.3 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Dehnung | 23.0 °C | 7 % Show Supplier Material materials with Dehnung of 7 % | ASTM D 638 | yld, Type I, 50 mm/min |
Hardness, Rockwell R | 23.0 °C | 118 [-] Show Supplier Material materials with Hardness, Rockwell R of 118 [-] | ASTM D 785 |
Härte, Rockwell M | 23.0 °C | 70 [-] Show Supplier Material materials with Härte, Rockwell M of 70 [-] | ASTM D 785 | |
Impact strength, Izod notched, ASTM | 23.0 °C | 801 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 801 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 3204 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 3204 J/m | ASTM D 4812 | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 801 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 801 kJ/m² | ASTM D 256 | notched, 23°C |
Zugfestigkeit | 23.0 °C | 62 MPa Show Supplier Material materials with Zugfestigkeit of 62 MPa | ASTM D 638 | yld, Type I, 50 mm/min |
Thermisch
Property | Temperature | Value | Comment |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 137 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 137 °C | ASTM D 648 | 6.4 mm, unannealed | |
Heat deflection temperature, 1.80 MPa | 132 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 132 °C | ASTM D 648 | 6.4 mm, unannealed | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 6.84E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 6.84E-5 1/K | ASTM E 831 | -40°C to 95°C |
Wärmeformbeständigkeitstemperatur | 132 - 137 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 132 - 137 °C |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 10.5 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 10.5 g/10min | ASTM D 1238 | 300°C/1.2 kgf | |
Schrumpfung | 23.0 °C | 0.5 % Show Supplier Material materials with Schrumpfung of 0.5 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Availability | Europe,Asia,MEA,Americas,Global | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |