Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.4 g/cm³ Show Supplier Material materials with Dichte of 1.4 g/cm³ | ASTM D 792 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 130 MPa Show Supplier Material materials with Biegefestigkeit of 130 MPa | ISO 178 | 2 mm/min |
Biegemodul | 23.0 °C | 6.4 GPa Show Supplier Material materials with Biegemodul of 6.4 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 2.5 % Show Supplier Material materials with Dehnung of 2.5 % | ISO 527 | break, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 6.9 GPa Show Supplier Material materials with Elastizitätsmodul of 6.9 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 80 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 80 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 450 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 450 J/m | ASTM D 4812 | 23°C |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 8 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 8 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 8 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 8 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 26 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 26 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 86 MPa Show Supplier Material materials with Zugfestigkeit of 86 MPa | ISO 527 | break, 5 mm/min |
Thermisch
Property | Value | Comment |
---|---|---|
Heat deflection temperature, 0.45 MPa | 124 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 124 °C | ASTM D 648 | 3.2 mm, unannealed |
Heat deflection temperature, 1.80 MPa | 118 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 118 °C | ASTM D 648 | 3.2mm, unannealed |
Wärmeformbeständigkeitstemperatur | 118 - 124 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 118 - 124 °C |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 10GHz | 23.0 °C | 3.32 [-] Show Supplier Material materials with Dielectric constant, 10GHz of 3.32 [-] | SABIC method |
Dielectric constant, 1GHz | 23.0 °C | 3.37 [-] Show Supplier Material materials with Dielectric constant, 1GHz of 3.37 [-] | SABIC method | 1.1 GHz |
Dielectric constant, 5GHz | 23.0 °C | 3.35 [-] Show Supplier Material materials with Dielectric constant, 5GHz of 3.35 [-] | SABIC method |
Dielektrizitätskonstante | 23.0 °C | 3.36 [-] Show Supplier Material materials with Dielektrizitätskonstante of 3.36 [-] | SABIC method | 1.9 GHz |
Dissipation factor, 1GHz | 23.0 °C | 8E-3 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 8E-3 [-] | SABIC method | |
Dissipation factor, 5GHz | 23.0 °C | 7E-3 [-] Show Supplier Material materials with Dissipation factor, 5GHz of 7E-3 [-] | SABIC method |
Verlustfaktor | 23.0 °C | 5E-3 [-] Show Supplier Material materials with Verlustfaktor of 5E-3 [-] | SABIC method |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 17 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 17 g/10min | ASTM D 1238 | 300°C/2.16 kgf | |
Schrumpfung | 23.0 °C | 0.2 % Show Supplier Material materials with Schrumpfung of 0.2 % | SABIC method |
Schrumpfung, diagonal | 23.0 °C | 0.2 % Show Supplier Material materials with Schrumpfung, diagonal of 0.2 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Wireless Communications, Wearables, Personal Computing, Electronic Components | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Time: 3 to 4.0hrs | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |