Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of friction | 0.22 - 0.24 [-] Show Supplier Material materials with Coefficient of friction of 0.22 - 0.24 [-] | ||
Coefficient of friction, kinetic | 0.24 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.24 [-] | ASTM D 3702 Modified: Manual | |
Coefficient of friction, static | 0.22 [-] Show Supplier Material materials with Coefficient of friction, static of 0.22 [-] | ASTM D 3702 Modified: Manual | |
Moisture absorption | 23.0 °C | 0.11 % Show Supplier Material materials with Moisture absorption of 0.11 % | ASTM D 570 | (23°C/50% RH/24 hrs) |
Relative Dichte | 23.0 °C | 1.3 [-] Show Supplier Material materials with Relative Dichte of 1.3 [-] | ASTM D 792 | |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 262 MPa Show Supplier Material materials with Biegefestigkeit of 262 MPa | ISO 178 | 2 mm/min |
Biegemodul | 23.0 °C | 20.6 GPa Show Supplier Material materials with Biegemodul of 20.6 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 1.6 % Show Supplier Material materials with Dehnung of 1.6 % | ISO 527 | break, 5 mm/min |
Druckfestigkeit | 23.0 °C | 128 MPa Show Supplier Material materials with Druckfestigkeit of 128 MPa | SABIC method |
Elastizitätsmodul | 23.0 °C | 23.8 GPa Show Supplier Material materials with Elastizitätsmodul of 23.8 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 94 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 94 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 504 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 504 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 16 J Show Supplier Material materials with Instrumented Impact, Total Energy of 16 J | ASTM D 3763 | 23°C |
Scherfestigkeit | 23.0 °C | 92 MPa Show Supplier Material materials with Scherfestigkeit of 92 MPa | ASTM D732 |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 9 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 33 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 33 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Schubmodule | 23.0 °C | 3.5 GPa Show Supplier Material materials with Schubmodule of 3.5 GPa | ASTM D732 |
Zugfestigkeit | 23.0 °C | 183 MPa Show Supplier Material materials with Zugfestigkeit of 183 MPa | ISO 527 | break, 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 130 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 130 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 9.7E-6 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 9.7E-6 1/K | ASTM D 696 | -30°C to 30°C |
Wärmeformbeständigkeitstemperatur | 130 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 130 °C | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 4.6E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 4.6E-5 1/K | ASTM D 696 | -30°C to 30°C |
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 1000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1000 Ω | ASTM D 257 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzvolumenflussrate | 28 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 28 cm³/10min | ASTM D 1238 | MVR at 300°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.05 % Show Supplier Material materials with Schrumpfung of 0.05 % | ASTM D 955 | 24 hrs |
Schrumpfung, diagonal | 23.0 °C | 0.15 % Show Supplier Material materials with Schrumpfung, diagonal of 0.15 % | ASTM D 955 | 24 hrs |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Pharmaceutical Packaging & Drug Delivery, Surgical Devices, Medical Device | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Temperature: 120°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |