Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.35 g/cm³ Show Supplier Material materials with Dichte of 1.35 g/cm³ | ASTM D 792 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 110 MPa Show Supplier Material materials with Biegefestigkeit of 110 MPa | ISO 178 | 2 mm/min |
Biegemodul | 23.0 °C | 4.1 GPa Show Supplier Material materials with Biegemodul of 4.1 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 3.5 % Show Supplier Material materials with Dehnung of 3.5 % | ISO 527 | break, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 4.6 GPa Show Supplier Material materials with Elastizitätsmodul of 4.6 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 100 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 100 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 600 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 600 J/m | ASTM D 4812 | 23°C |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 9 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 60 MPa Show Supplier Material materials with Zugfestigkeit of 60 MPa | ISO 527 | break, 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 126 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 126 °C | ASTM D 648 | 3.2 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 120 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 120 °C | ASTM D 648 | 3.2mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 3.5E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 3.5E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Wärmeformbeständigkeitstemperatur | 120 - 126 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 120 - 126 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 6.7E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 6.7E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Entflammbarkeit | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103895096- - <br> UL Recognized, 94V-0 Flame Class Rating: 0.8mm UL 94 | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielectric constant, 10GHz | 23.0 °C | 3.17 [-] Show Supplier Material materials with Dielectric constant, 10GHz of 3.17 [-] | SABIC method |
Dielectric constant, 1GHz | 23.0 °C | 3.15 [-] Show Supplier Material materials with Dielectric constant, 1GHz of 3.15 [-] | SABIC method | 1.1 GHz |
Dielectric constant, 5GHz | 23.0 °C | 3.15 [-] Show Supplier Material materials with Dielectric constant, 5GHz of 3.15 [-] | SABIC method |
Dielektrizitätskonstante | 23.0 °C | 3.04 [-] Show Supplier Material materials with Dielektrizitätskonstante of 3.04 [-] | SABIC method | 20 GHz |
Dissipation factor, 1GHz | 23.0 °C | 0.01 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 0.01 [-] | SABIC method | |
Dissipation factor, 5GHz | 23.0 °C | 0.01 [-] Show Supplier Material materials with Dissipation factor, 5GHz of 0.01 [-] | SABIC method |
Verlustfaktor | 23.0 °C | 0.01 [-] Show Supplier Material materials with Verlustfaktor of 0.01 [-] | SABIC method | 20 GHz |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 11 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 11 g/10min | ASTM D 1238 | 300°C/1.2 kgf | |
Schrumpfung | 23.0 °C | 0.2 % Show Supplier Material materials with Schrumpfung of 0.2 % | SABIC method |
Schrumpfung, diagonal | 23.0 °C | 0.3 % Show Supplier Material materials with Schrumpfung, diagonal of 0.3 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Electronic Components, Personal Computing, Wearables, Wireless Communications | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Temperature: 110°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |