Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.27 g/cm³ Show Supplier Material materials with Dichte of 1.27 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.04 % Show Supplier Material materials with Wasserabsorption of 0.04 % | ISO 62-1 | (23°C/24hrs) |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 132 MPa Show Supplier Material materials with Biegefestigkeit of 132 MPa | ISO 178 | break, 2 mm/min |
Biegemodul | 23.0 °C | 4.2 GPa Show Supplier Material materials with Biegemodul of 4.2 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 3.6 % Show Supplier Material materials with Dehnung of 3.6 % | ISO 527 | break, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 4.4 GPa Show Supplier Material materials with Elastizitätsmodul of 4.4 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 140 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 140 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 700 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 700 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 21 J Show Supplier Material materials with Instrumented Impact, Total Energy of 21 J | ASTM D 3763 | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 140 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 140 kJ/m² | ASTM D 256 | notched, 23°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 42 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 42 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 82 MPa Show Supplier Material materials with Zugfestigkeit of 82 MPa | ISO 527 | break, 5 mm/min |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | ||||
Glow Wire Ignition Temperature | 850 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 850 °C | IEC 60695-2-13 | 1.6 mm | |||
Heat deflection temperature, 0.45 MPa | 121 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 121 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 115 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 115 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 4E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 4E-5 1/K | ASTM E 831 | 23°C to 80°C | ||
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Vicat-Erweichungstemperatur | 123 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 123 °C | ISO 306 | Rate B/50 | |||
Wärmeformbeständigkeitstemperatur | 115 - 121 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 115 - 121 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 8.3E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 8.3E-5 1/K | ASTM E 831 | 23°C to 80°C | ||
Entflammbarkeit | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103129464- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.6mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.5mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.5mm UL 94 <br> Glow Wire Ignitability Temperature, 1.0 mm: 850°C IEC 60695-2-13 <br> Glow Wire Flammability Index, 1.0 mm: 960°C IEC 60695-2-12 <br> Glow Wire Flammability Index, 1.6 mm: 960°C IEC 60695-2-12 |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 10GHz | 23.0 °C | 3.05 [-] Show Supplier Material materials with Dielectric constant, 10GHz of 3.05 [-] | SABIC method |
Dielectric constant, 1GHz | 23.0 °C | 3.03 [-] Show Supplier Material materials with Dielectric constant, 1GHz of 3.03 [-] | SABIC method | 1.1 GHz |
Dielectric constant, 5GHz | 23.0 °C | 3.05 [-] Show Supplier Material materials with Dielectric constant, 5GHz of 3.05 [-] | SABIC method |
Dielektrizitätskonstante | 23.0 °C | 3.04 [-] Show Supplier Material materials with Dielektrizitätskonstante of 3.04 [-] | SABIC method | 1.9 GHz |
Dissipation factor, 1GHz | 23.0 °C | 6.4E-3 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 6.4E-3 [-] | SABIC method | |
Dissipation factor, 5GHz | 23.0 °C | 6.2E-3 [-] Show Supplier Material materials with Dissipation factor, 5GHz of 6.2E-3 [-] | SABIC method |
Kriechstromfestigkeit | 23.0 °C | 3 V Show Supplier Material materials with Kriechstromfestigkeit of 3 V | UL 746A | (UL) {PLC} |
Sheet resistivity, ROA | 23.0 °C | 1.00E+16 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+16 Ω | >, ASTM D 257 |
Verlustfaktor | 23.0 °C | 6.3E-3 [-] Show Supplier Material materials with Verlustfaktor of 6.3E-3 [-] | SABIC method |
Volume resistivity | 23.0 °C | 1.00E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+16 Ω·cm | >, ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 24 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 24 g/10min | ASTM D 1238 | 300°C/2.16 kgf | |
Schmelzvolumenflussrate | 11 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 11 cm³/10min | ISO 1133 | MVR at 300°C/1.2 kg | |
Schrumpfung | 23.0 °C | 0.3 % Show Supplier Material materials with Schrumpfung of 0.3 % | ASTM D 955 | 24 hrs |
Schrumpfung, diagonal | 23.0 °C | 0.3 % Show Supplier Material materials with Schrumpfung, diagonal of 0.3 % | ASTM D 955 | 24 hrs |
Technological properties
Property | ||
---|---|---|
Application areas | Enclosure/Housing/Cover | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 110°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |