FLEX NORYL™ Resin WCV072 - Asia

Want to keep this datasheet? Save it now in your required format

Description

FLEX NORYL™ WCV072 resin is a flexible, non-reinforced extrusion grade of Polyphenylene Ether (PPE) + Thermoplastic Elastomer (TPE) with a Shore D Hardness rating of 72. FLEX NORYL WCV072 resin was developed for evaluation in automotive wire + cable applications requiring ISO6722 Class A or B. It exhibits ultra-thin wall capability, good scratch abrasion and pinch resistance, high dimensional stability, low shrinkage and warpage, very low water absorption, chemical resistance, and good dielectric strength. Processing is typically conducted on standard extrusion equipment, and UL 1581 testing is conducted on 2.0mm wire with 0.12mm X 20 stranded copper conductor.

Diese Materialdaten wurden von Sabic zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Anwendungen

Elektrotechnik

Automobil

Allgemeine Fahrzeugteile

Fahrzeugaußenbereich

Materialien von diesem Anbieter

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

Sehen Sie alle Materialen dieses Anbieters

Eigenschaften

Allgemein

Property	Temperature	Value	Comment
Dichte	23.0 °C	1.03 g/cm³ Show Supplier Material materials with Dichte of 1.03 g/cm³	ISO 1183
Moisture absorption	23.0 °C	0.05 % Show Supplier Material materials with Moisture absorption of 0.05 %	ISO 62 \| (23°C / 50% RH)
Relative Dichte	23.0 °C	1.03 [-] Show Supplier Material materials with Relative Dichte of 1.03 [-]	ASTM D 792
Wasserabsorption	23.0 °C	0.12 % Show Supplier Material materials with Wasserabsorption of 0.12 %	ISO 62-1 \| (23°C/saturated)

Mechanisch

Property	Temperature	Value	Comment
Biegefestigkeit	23.0 °C	59 MPa Show Supplier Material materials with Biegefestigkeit of 59 MPa	ISO 178 \| yield, 2 mm/min
Biegemodul	23.0 °C	1.7 GPa Show Supplier Material materials with Biegemodul of 1.7 GPa	ISO 178 \| 2 mm/min
Dehnung	23.0 °C	46 % Show Supplier Material materials with Dehnung of 46 %	ISO 527 \| break, 50 mm/min
Elastizitätsmodul	23.0 °C	1.8 GPa Show Supplier Material materials with Elastizitätsmodul of 1.8 GPa	ISO 527 \| 1 mm/min
Impact strength, Izod notched, ASTM	23.0 °C	309 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 309 J/m	ASTM D 256
Instrumented Impact, Total Energy	23.0 °C	45 J Show Supplier Material materials with Instrumented Impact, Total Energy of 45 J	ASTM D 3763 \| 23°C
Schlagfestigkeit, Charpy gekerbt	23.0 °C	33 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 33 kJ/m²	ISO 179/1eA \| V-notch Edgew, 23°C, 80104 sp=62mm
Schlagzähigkeit, Izod gekerbt	23.0 °C	6 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 6 kJ/m²	ISO 180/1A \| 80104, -30°C
Zugfestigkeit	23.0 °C	44 MPa Show Supplier Material materials with Zugfestigkeit of 44 MPa	ISO 527 \| yield, 50 mm/min

Thermisch

Property	Temperature	Value	Comment
Heat deflection temperature, 1.80 MPa		98 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 98 °C	ISO 75/Af \| Flatw 80104 sp=64mm
Koeffizient der thermischen Ausdehnung	23.0 °C	8.4E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 8.4E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Vicat-Erweichungstemperatur		117 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 117 °C	ISO 306 \| Rate B/120
Wärmeformbeständigkeitstemperatur		98 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 98 °C
thermischer Ausdehnungskoeffizient, transversal	23.0 °C	1.11E-4 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.11E-4 1/K	ISO 11359-2 \| -40°C to 40°C

Rheological Properties

Property	Value	Comment
Schmelzmassenflussrate	13.8 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 13.8 g/10min	ASTM D 1238 \| 280°C/5.0 kgf
Schmelzvolumenflussrate	13 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 13 cm³/10min	ISO 1133 \| MVR at 280°C/5.0 kg

Technological properties

Property
Application areas	Auto Electrical, Auto Aftermarket, Wire & cable
Availability	Europe,Asia,Americas
Processing methods	Head Zone Temperature: 250 to 285.0°C Drying Time (Cumulative): 12hrs Water Bath Temperature: 15 to 80.0°C Neck Temperature: 250 to 285.0°C Middle Zone Temperatures: 230 to 285.0°C Melt Temperature: 250 to 285.0°C Screw Speed: 15 to 40.0rpm Screen Pack: 150 to 100.0- Feed Zone Temperature: 210 to 260.0°C Drying Time: 4 to 6.0hrs Conductor Pre-heat Temperature: 80 to 150.0°C Die Temperature: 250 to 285.0°C Drying Temperature: 60 to 80.0°C Cross-head Temperature: 250 to 285.0°C Cooling Water Air Gap: 100 to 200.0mm Maximum Moisture Content: 0.02% Extruder Length/Diameter Ratio (L/D): 22:1 to 26:1-
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.