FLEX NORYL™ Resin WCV063 - Asia

Want to keep this datasheet? Save it now in your required format

Description

FLEX NORYL™ WCV063 resin is a flexible, non-reinforced extrusion grade of Polyphenylene Ether (PPE) + Thermoplastic Elastomer (TPE) with a Shore D Hardness rating of 63. FLEX NORYL WCV063 resin was developed for evaluation in automotive wire + cable applications requiring ISO6722 Class A or B. It exhibits ultra-thin wall capability, good scratch abrasion and pinch resistance, high dimensional stability, low shrinkage and warpage, very low water absorption, chemical resistance, and good dielectric strength. Processing is typically conducted on standard extrusion equipment, and UL 1581 testing is conducted on 2.0mm wire with 0.12mm X 20 stranded copper conductor.

Diese Materialdaten wurden von Sabic zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Anwendungen

Elektrotechnik

Automobil

Allgemeine Fahrzeugteile

Automotive Interior

Materialien von diesem Anbieter

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

Sehen Sie alle Materialen dieses Anbieters

Eigenschaften

Allgemein

Property	Temperature	Value	Comment
Relative Dichte	23.0 °C	1.03 [-] Show Supplier Material materials with Relative Dichte of 1.03 [-]	ASTM D 792

Mechanisch

Property	Temperature	Value	Comment
Biegemodul	23.0 °C	0.8 GPa Show Supplier Material materials with Biegemodul of 0.8 GPa	ISO 178
Dehnung	23.0 °C	50 % Show Supplier Material materials with Dehnung of 50 %	ISO 527 \| break, 50 mm/min
Elastizitätsmodul	23.0 °C	0.7 GPa Show Supplier Material materials with Elastizitätsmodul of 0.7 GPa	ISO 527 \| 1 mm/min
Härte, Shore D	23.0 °C	63 [-] Show Supplier Material materials with Härte, Shore D of 63 [-]	ASTM D 2240 \| 10S reading
Impact strength, Izod notched, ASTM	23.0 °C	170 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 170 J/m	ASTM D 256 \| notched, -30°C
Schlagzähigkeit, Izod gekerbt	23.0 °C	37 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 37 kJ/m²	ISO 180/1A \| 80104, 23°C
Zugfestigkeit	23.0 °C	25 MPa Show Supplier Material materials with Zugfestigkeit of 25 MPa	ISO 527 \| yield

Thermisch

Property	Value	Comment
Heat deflection temperature, 0.45 MPa	82 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 82 °C	ASTM D 648 \| 3.2 mm, unannealed
Heat deflection temperature, 1.80 MPa	66 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 66 °C	ISO 75/Af \| Flatw 80104 sp=64mm
Wärmeformbeständigkeitstemperatur	66 - 82 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 66 - 82 °C

Elektrisch

Property	Temperature	Value	Comment
Dielectric constant, 1GHz	23.0 °C	2.47 [-] Show Supplier Material materials with Dielectric constant, 1GHz of 2.47 [-]	ASTM D 150
Dissipation factor, 1GHz	23.0 °C	3.2E-3 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 3.2E-3 [-]	ASTM D 150

Rheological Properties

Property	Value	Comment
Schmelzmassenflussrate	33 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 33 g/10min	ASTM D 1238 \| 280°C/5.0 kgf

Technological properties

Property
Application areas	Airbag, Auto Electrical, Wire & cable
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 80 to 100.0°C Die Temperature: 280 to 300.0°C Extruder Length/Diameter Ratio (L/D): >24:1- Drying Time (Cumulative): 8hrs Neck Temperature: 280 to 300.0°C Melt Temperature: 280 to 300.0°C Drying Time: 4 to 6.0hrs Middle Zone Temperatures: 270 to 300.0°C Cooling Water Air Gap: 100 to 1000.0mm Conductor Pre-heat Temperature: 100 to 150.0°C Screw Speed: 5 to 60.0rpm Water Bath Temperature: 15 to 30.0°C Maximum Moisture Content: 0.02% Cross-head Temperature: 280 to 300.0°C Head Zone Temperature: 280 to 300.0°C Feed Zone Temperature: 200 to 260.0°C Screen Pack: 60/200/60- Compression Ratio: 2:1-3:1-
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.