Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.19 g/cm³ Show Supplier Material materials with Dichte of 1.19 g/cm³ | ISO 1183 |
Sauerstoffindex | 23.0 °C | 28 % Show Supplier Material materials with Sauerstoffindex of 28 % | |
Wasserabsorption | 23.0 °C | 5.5 % Show Supplier Material materials with Wasserabsorption of 5.5 % | ISO 62-1 | (23°C/saturated) |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 230 MPa Show Supplier Material materials with Biegefestigkeit of 230 MPa | ISO 178 | break, 2 mm/min |
Biegemodul | 23.0 °C | 10 GPa Show Supplier Material materials with Biegemodul of 10 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 2 % Show Supplier Material materials with Dehnung of 2 % | ISO 527 | break, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 13 GPa Show Supplier Material materials with Elastizitätsmodul of 13 GPa | ISO 527 | 1 mm/min |
Hardness, Rockwell L | 23.0 °C | 105 [-] Show Supplier Material materials with Hardness, Rockwell L of 105 [-] | ISO 2039-2 |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 5 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 170 MPa Show Supplier Material materials with Zugfestigkeit of 170 MPa | ISO 527 | break, 5 mm/min |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 252 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 252 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |||
Heat deflection temperature, 1.80 MPa | 250 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 250 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 2E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 2E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Vicat-Erweichungstemperatur | 255 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 255 °C | ISO 306 | Rate B/120 | |||
Wärmeformbeständigkeitstemperatur | 250 - 252 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 250 - 252 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.1E-4 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.1E-4 1/K | ISO 11359-2 | 23°C to 60°C | ||
Entflammbarkeit | UL Compliant, 94HB Flame Class Rating: 1.6mm UL 94 by SABIC-IP |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 178000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 178000 Ω | IEC 60093 |
Volume resistivity | 23.0 °C | 178000 Ω·cm Show Supplier Material materials with Volume resistivity of 178000 Ω·cm | IEC 60093 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schrumpfung | 23.0 °C | 0.1 % Show Supplier Material materials with Schrumpfung of 0.1 % | SABIC method | on tensile bar |
Technological properties
Property | ||
---|---|---|
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |