Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.2 g/cm³ Show Supplier Material materials with Dichte of 1.2 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.35 % Show Supplier Material materials with Moisture absorption of 0.35 % | ISO 62 | (23°C / 50% RH) |
Relative Dichte | 23.0 °C | 1.2 [-] Show Supplier Material materials with Relative Dichte of 1.2 [-] | ASTM D 792 | |
Specific volume | 23.0 °C | 0.83 cm³/g Show Supplier Material materials with Specific volume of 0.83 cm³/g | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.16 % Show Supplier Material materials with Wasserabsorption of 0.16 % | ISO 62-1 | (23°C/saturated) |
Mechanisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Biegefestigkeit | 23.0 °C | 66 MPa Show Supplier Material materials with Biegefestigkeit of 66 MPa | ISO 178 | yield, 2 mm/min | ||
Biegemodul | 23.0 °C | 2.1 GPa Show Supplier Material materials with Biegemodul of 2.1 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 85 % Show Supplier Material materials with Dehnung of 85 % | ISO 527 | break, 50 mm/min | ||
Elastizitätsmodul | 23.0 °C | 2.2 GPa Show Supplier Material materials with Elastizitätsmodul of 2.2 GPa | ISO 527 | 1 mm/min | ||
Hardness, Rockwell R | 23.0 °C | 122 [-] Show Supplier Material materials with Hardness, Rockwell R of 122 [-] | ASTM D 785 | ||
Härte, Rockwell M | 23.0 °C | 85 [-] Show Supplier Material materials with Härte, Rockwell M of 85 [-] | ASTM D 785 | | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 600 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 600 J/m | ASTM D 256 | ||
Instrumented Impact, Total Energy | 23.0 °C | 120 J Show Supplier Material materials with Instrumented Impact, Total Energy of 120 J | ASTM D 3763 | 23°C | ||
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 13 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 13 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, -30°C | ||
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 53 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 53 kJ/m² | ISO 180/1A | 80*10*3, 23°C | ||
Zugfestigkeit | 23.0 °C | 60 MPa Show Supplier Material materials with Zugfestigkeit of 60 MPa | ISO 527 | break, 50 mm/min | ||
Impact strength, Izod unnotched, ASTM | ASTM D 4812 | 23°C | ||||
Schlagzähigkeit, Charpy ungekerbt | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm, -30°C | ||||
Schlagzähigkeit, Izod ungekerbt | ISO 180/1U | 80*10*3, 23°C |
Thermisch
Property | Temperature | Value | Comment |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 125 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 125 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 6E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 6E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Spezifische Wärmekapazität | 23.0 °C | 1.25E-3 J/(kg·K) Show Supplier Material materials with Spezifische Wärmekapazität of 1.25E-3 J/(kg·K) | ASTM C 351 |
Vicat-Erweichungstemperatur | 154 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 154 °C | ISO 306 | Rate B/50 | |
Wärmeformbeständigkeitstemperatur | 125 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 125 °C | ||
Wärmeleitfähigkeit | 23.0 °C | 0.21 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 0.21 W/(m·K) | ASTM C177 |
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 6E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 6E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 60Hz | 23.0 °C | 3.15 [-] Show Supplier Material materials with Dielectric constant, 60Hz of 3.15 [-] | ASTM D 150 | 50/60 Hz |
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 3 [-] Show Supplier Material materials with Dielektrizitätskonstante, 1 MHz of 3 [-] | ASTM D 150 |
Dissipation factor, 100Hz | 23.0 °C | 0.02 [-] Show Supplier Material materials with Dissipation factor, 100Hz of 0.02 [-] | ASTM D 150 |
Dissipation factor, 50Hz | 23.0 °C | 1.2E-3 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 1.2E-3 [-] | ASTM D 150 | 50/60 Hz |
Durchschlagfestigkeit | 23.0 °C | 20.2 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 20.2 kV/mm | ASTM D 149 | in air, 3.2 mm |
Volume resistivity | 23.0 °C | 2.60E+17 Ω·cm Show Supplier Material materials with Volume resistivity of 2.60E+17 Ω·cm | >, ASTM D 257 |
Optisch
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 6 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 6 g/10min | ASTM D 1238 | 300°C/1.2 kgf | |
Schmelzvolumenflussrate | 29 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 29 cm³/10min | ISO 1133 | MVR at 330°C/2.16kg | |
Schrumpfung | 23.0 °C | 0.6 % Show Supplier Material materials with Schrumpfung of 0.6 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Surgical Devices, Renal and Blood Handling, Pharmaceutical Manufacturing, Pharmaceutical Packaging & Drug Delivery, Medical Device | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |