Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Moisture absorption | 23.0 °C | 0.05 % Show Supplier Material materials with Moisture absorption of 0.05 % | ISO 62 | (23°C / 50% RH) |
Relative Dichte | 23.0 °C | 1.2 [-] Show Supplier Material materials with Relative Dichte of 1.2 [-] | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.1 % Show Supplier Material materials with Wasserabsorption of 0.1 % | ISO 62-1 | (23°C/saturated) |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 90 MPa Show Supplier Material materials with Biegefestigkeit of 90 MPa | ISO 178 | break, 2 mm/min |
Biegemodul | 23.0 °C | 2.5 GPa Show Supplier Material materials with Biegemodul of 2.5 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 64 % Show Supplier Material materials with Dehnung of 64 % | ISO 527 | break, 50 mm/min |
Elastizitätsmodul | 23.0 °C | 2.4 GPa Show Supplier Material materials with Elastizitätsmodul of 2.4 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 700 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 700 J/m | ASTM D 256 |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 51 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 51 kJ/m² | ISO 179/1eA | 80*10*4mm, Cut, 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 700 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 700 kJ/m² | ASTM D 256 | notched, 23°C |
Zugfestigkeit | 23.0 °C | 63 MPa Show Supplier Material materials with Zugfestigkeit of 63 MPa | ISO 527 | yield, 50 mm/min |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 101 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 101 °C | ASTM D 648 | 3.2 mm, unannealed | |
Heat deflection temperature, 1.80 MPa | 92 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 92 °C | ASTM D 648 | 3.2mm, unannealed | |
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |
Vicat-Erweichungstemperatur | 116 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 116 °C | ISO 306 | Rate B/120 | |
Wärmeformbeständigkeitstemperatur | 92 - 101 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 92 - 101 °C | ||
Entflammbarkeit | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103823841- - <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.25mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.25mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.6mm UL 94 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 18 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 18 g/10min | ASTM D 1238 | 260°C/2.16 kgf | |
Schmelzvolumenflussrate | 18 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 18 cm³/10min | ISO 1133 | MVR at 260°C/2.16 kg | |
Schrumpfung | 23.0 °C | 0.3 % Show Supplier Material materials with Schrumpfung of 0.3 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.4 % Show Supplier Material materials with Schrumpfung, diagonal of 0.4 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Personal Computing, Power Manangement, Wireless Communications, Watch/Jewelry | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 80 to 90.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |