Eigenschaften
Allgemein
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 65 MPa Show Supplier Material materials with Biegefestigkeit of 65 MPa | ISO 178 |
Biegemodul | 23.0 °C | 2.1 GPa Show Supplier Material materials with Biegemodul of 2.1 GPa | ISO 178 |
Dehnung | 23.0 °C | 60 % Show Supplier Material materials with Dehnung of 60 % | ISO 527 | break |
Elastizitätsmodul | 23.0 °C | 2.1 GPa Show Supplier Material materials with Elastizitätsmodul of 2.1 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 453 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 453 J/m | ASTM D 256 |
Instrumented Impact, Total Energy | 23.0 °C | 42 J Show Supplier Material materials with Instrumented Impact, Total Energy of 42 J | ASTM D 3763 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 36 J Show Supplier Material materials with Instrumented Impact, at Peak of 36 J | ASTM D 3763 | 23°C |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 33 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 33 kJ/m² | ISO 179/2C | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 15 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 15 kJ/m² | ISO 180/1A | notched 80*10*4, -30°C |
Zugfestigkeit | 23.0 °C | 40 MPa Show Supplier Material materials with Zugfestigkeit of 40 MPa | ISO 527 | break |
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 126 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 126 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 110 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 110 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.17E-4 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.17E-4 1/K | ASTM E 831 | 0°C to 100°C |
Vicat-Erweichungstemperatur | 119 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 119 °C | ISO 306 | Rate B/50 | |
Wärmeformbeständigkeitstemperatur | 110 - 126 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 110 - 126 °C |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 15 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 15 g/10min | ASTM D 1238 | 280°C/5.0 kgf | |
Schmelzvolumenflussrate | 15 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 15 cm³/10min | ISO 1133 | MVR at 280°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.5 % Show Supplier Material materials with Schrumpfung of 0.5 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Tray, Recreational Vehicle, Document Handling, Forward Lighting | |
| Availability | Europe,Americas | |
| Processing methods | Drying Temperature: 95 to 105.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |