Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.2 g/cm³ Show Supplier Material materials with Dichte of 1.2 g/cm³ | ISO 1183 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 110 MPa Show Supplier Material materials with Biegefestigkeit of 110 MPa | ISO 178 | break, 2 mm/min |
Biegemodul | 23.0 °C | 4 GPa Show Supplier Material materials with Biegemodul of 4 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 4 % Show Supplier Material materials with Dehnung of 4 % | ISO 527 | break, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 4.2 GPa Show Supplier Material materials with Elastizitätsmodul of 4.2 GPa | ISO 527 | 1 mm/min |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 3 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 3 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 35 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 35 kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 4 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 4 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 40 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 40 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 65 MPa Show Supplier Material materials with Zugfestigkeit of 65 MPa | ISO 527 | break, 5 mm/min |
Thermisch
Property | Temperature | Value | Comment |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 185 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 185 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 5E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 5E-5 1/K | ISO 11359-2 | 23°C to 60°C |
Vicat-Erweichungstemperatur | 200 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 200 °C | ISO 306 | Rate B/120 | |
Wärmeformbeständigkeitstemperatur | 185 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 185 °C | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 6.5E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 6.5E-5 1/K | ISO 11359-2 | 23°C to 60°C |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Volume resistivity | 23.0 °C | 1000 - 10000 Ω·cm Show Supplier Material materials with Volume resistivity of 1000 - 10000 Ω·cm | SABIC method |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzvolumenflussrate | 10 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 10 cm³/10min | ISO 1133 | MVR at 280°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.8 % Show Supplier Material materials with Schrumpfung of 0.8 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Exterior Trim, Fuel Handling | |
Availability | Europe,Asia,Americas | |
Processing methods | Middle - Zone 2 Temperature: 270 to 290.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |