Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.06 g/cm³ Show Supplier Material materials with Dichte of 1.06 g/cm³ | ASTM D 792 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 85 MPa Show Supplier Material materials with Biegefestigkeit of 85 MPa | ASTM D 790 |
Biegemodul | 23.0 °C | 11 GPa Show Supplier Material materials with Biegemodul of 11 GPa | ASTM D 790 |
Dehnung | 23.0 °C | 0.5 % Show Supplier Material materials with Dehnung of 0.5 % | ASTM D 638 | break |
Impact strength, Izod notched, ASTM | 23.0 °C | 41 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 41 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 213 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 213 J/m | ASTM D 4812 | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 58 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 58 kJ/m² | ASTM D 256 | notched, 23°C |
Zugfestigkeit | 23.0 °C | 59 MPa Show Supplier Material materials with Zugfestigkeit of 59 MPa | ASTM D 638 | break |
Technological properties
Property | ||
---|---|---|
Application areas | Personal Computing | |
Availability | Asia,Americas | |
Processing methods | Back Pressure: 0.2 to 0.3MPa | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |