| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.18 g/cm³ Show Supplier Material materials with Dichte of 1.18 g/cm³ | ASTM D 792 |
Moisture absorption | 23.0 °C | 0.43 % Show Supplier Material materials with Moisture absorption of 0.43 % | ISO 62 | (23°C / 50% RH) |
Relative Dichte | 23.0 °C | 1.19 [-] Show Supplier Material materials with Relative Dichte of 1.19 [-] | ASTM D 792 | |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegefestigkeit | 23.0 °C | 93 MPa Show Supplier Material materials with Biegefestigkeit of 93 MPa | ISO 178 | break, 2 mm/min | ||
Biegemodul | 23.0 °C | 2.3 GPa Show Supplier Material materials with Biegemodul of 2.3 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 46.7 % Show Supplier Material materials with Dehnung of 46.7 % | ISO 527 | break | ||
Elastizitätsmodul | 23.0 °C | 2.3 GPa Show Supplier Material materials with Elastizitätsmodul of 2.3 GPa | ISO 527 | 1 mm/min | ||
Hardness, Rockwell L | 23.0 °C | 92.2 [-] Show Supplier Material materials with Hardness, Rockwell L of 92.2 [-] | ASTM D 785 | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 753 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 753 J/m | ASTM D 256 | ||
Instrumented Impact, Total Energy | 23.0 °C | 62.5 J Show Supplier Material materials with Instrumented Impact, Total Energy of 62.5 J | ASTM D 3763 | 23°C | ||
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 12.9 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 12.9 kJ/m² | ISO 179/2C | -30°C | ||
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 51.3 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 51.3 kJ/m² | ISO 180/1A | 80*10*4, 23°C | ||
Zugfestigkeit | 23.0 °C | 47 MPa Show Supplier Material materials with Zugfestigkeit of 47 MPa | ISO 527 | break | ||
Impact strength, Izod unnotched, ASTM | ASTM D 4812 | 23°C | ||||
Schlagzähigkeit, Charpy ungekerbt | ISO 179/2C | 23°C | ||||
Schlagzähigkeit, Izod ungekerbt | ISO 180/1U | unnotched 80*10*4, 23°C | ||||
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 112 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 112 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 103 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 103 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 6.5E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 6.5E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Vicat-Erweichungstemperatur | 119 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 119 °C | ISO 306 | Rate B/120 | |||
Wärmeformbeständigkeitstemperatur | 103 - 112 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 103 - 112 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 6.6E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 6.6E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Entflammbarkeit | UL Recognized, 94V-1 Flame Class Rating: ≥0.8mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥1.2mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103826700- - | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielectric constant, 1GHz | 23.0 °C | 2.83 [-] Show Supplier Material materials with Dielectric constant, 1GHz of 2.83 [-] | SABIC method | 1.1 GHz |
Dissipation factor, 1GHz | 23.0 °C | 6.1E-3 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 6.1E-3 [-] | SABIC method | |
Sheet resistivity, ROA | 23.0 °C | 1.00E+16 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+16 Ω | >, ASTM D 257 |
Volume resistivity | 23.0 °C | 1.00E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+16 Ω·cm | >, ASTM D 257 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 20 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 20 g/10min | ASTM D 1238 | 300°C/1.2 kgf | |
Schrumpfung | 23.0 °C | 0.6 % Show Supplier Material materials with Schrumpfung of 0.6 % | ASTM D 955 | 24 hrs |
Schrumpfung, diagonal | 23.0 °C | 0.62 % Show Supplier Material materials with Schrumpfung, diagonal of 0.62 % | ASTM D 955 | 24 hrs |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Wiring Devices, Wireless Communications, Monitoring and Imaging, Power Manangement, Industrial Material Handling, Electronics, Enclosures, Electronic Components | |
| Availability | Asia | |
| Processing methods | Drying Temperature: 100°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |