Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.49 g/cm³ Show Supplier Material materials with Dichte of 1.49 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.98 % Show Supplier Material materials with Moisture absorption of 0.98 % | ASTM D 570 | (23°C/50% RH/24 hrs) |
Relative Dichte | 23.0 °C | 1.49 [-] Show Supplier Material materials with Relative Dichte of 1.49 [-] | ASTM D 792 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Elastizitätsmodul | 23.0 °C | 12.9 GPa Show Supplier Material materials with Elastizitätsmodul of 12.9 GPa | ISO 527 | 1 mm/min |
Härte, Rockwell M | 23.0 °C | 92 [-] Show Supplier Material materials with Härte, Rockwell M of 92 [-] | ASTM D 785 | |
Impact strength, Izod notched, ASTM | 23.0 °C | 94 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 94 J/m | ASTM D 256 | notched, 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 7 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 7 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 168 MPa Show Supplier Material materials with Zugfestigkeit of 168 MPa | ISO 527 | break, 5 mm/min |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 224 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 224 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Relative temperature index, electrical | 130 °C Show Supplier Material materials with Relative temperature index, electrical of 130 °C | UL 746B | |
Relative temperature index, mechanical impact | 105 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | |
Relative temperature index, mechanical strength | 115 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 115 °C | UL 746B | |
Wärmeformbeständigkeitstemperatur | 224 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 224 °C | ||
Entflammbarkeit | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101281596- - <br> UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
High Amp Arc Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm | ≥, UL 746A | PLC 1 |
High Volt Arc Track Rate | 23.0 °C | 0 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 0 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm | ≥, UL 746A | PLC 4 |
Technological properties
Property | ||
---|---|---|
Application areas | Modular Panel | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 80°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |