Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Relative Dichte | 23.0 °C | 1.31 [-] Show Supplier Material materials with Relative Dichte of 1.31 [-] | ASTM D 792 |
Specific volume | 23.0 °C | 0.76 cm³/g Show Supplier Material materials with Specific volume of 0.76 cm³/g | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.08 % Show Supplier Material materials with Wasserabsorption of 0.08 % | ASTM D 570 | (23°C/24hrs) |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 82 MPa Show Supplier Material materials with Biegefestigkeit of 82 MPa | ASTM D 790 | yld, 1.3 mm/min, 50 mm span |
Biegemodul | 23.0 °C | 2.3 GPa Show Supplier Material materials with Biegemodul of 2.3 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Dehnung | 23.0 °C | 200 % Show Supplier Material materials with Dehnung of 200 % | ASTM D 638 | brk, Type I, 50 mm/min |
Gardner Impact | 23.0 °C | 40 J Show Supplier Material materials with Gardner Impact of 40 J | ASTM D 3029 | modified, 23°C |
Hardness, Rockwell R | 23.0 °C | 117 [-] Show Supplier Material materials with Hardness, Rockwell R of 117 [-] | ASTM D 785 |
Impact strength, Izod notched, ASTM | 23.0 °C | 53 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 53 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 1602 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 1602 J/m | ASTM D 4812 | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 53 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 53 kJ/m² | ASTM D 256 | notched, 23°C |
Zugfestigkeit | 23.0 °C | 51 MPa Show Supplier Material materials with Zugfestigkeit of 51 MPa | ASTM D 638 | brk, Type I, 50 mm/min |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 154 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 154 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 54 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 54 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.39E-4 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.39E-4 1/K | ASTM E 831 | 60°C to 138°C | ||
Relative temperature index, electrical | 120 °C Show Supplier Material materials with Relative temperature index, electrical of 120 °C | UL 746B | |||
Relative temperature index, mechanical impact | 120 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 120 °C | UL 746B | |||
Relative temperature index, mechanical strength | 140 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | |||
Wärmeformbeständigkeitstemperatur | 54 - 154 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 54 - 154 °C | ||||
Entflammbarkeit | UL Recognized, 94HB Flame Class Rating: ≥0.84mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103952988- - |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 3.1 [-] Show Supplier Material materials with Dielektrizitätskonstante, 1 MHz of 3.1 [-] | ASTM D 150 |
Dielektrizitätskonstante, 100 Hz | 23.0 °C | 3.3 [-] Show Supplier Material materials with Dielektrizitätskonstante, 100 Hz of 3.3 [-] | ASTM D 150 |
Dissipation factor, 100Hz | 23.0 °C | 2E-3 [-] Show Supplier Material materials with Dissipation factor, 100Hz of 2E-3 [-] | ASTM D 150 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 0.02 [-] | ASTM D 150 |
Durchschlagfestigkeit | 23.0 °C | 15.7 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 15.7 kV/mm | ASTM D 149 | in oil, 3.2 mm |
High Amp Arc Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm | ≥, UL 746A | PLC 0 |
High Volt Arc Track Rate | 23.0 °C | 1 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 1 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm | ≥, UL 746A | PLC 4 |
Kriechstromfestigkeit | 23.0 °C | 0 V Show Supplier Material materials with Kriechstromfestigkeit of 0 V | UL 746A | (UL) {PLC} |
Volume resistivity | 23.0 °C | 4.00E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 4.00E+16 Ω·cm | >, ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt viscosity | 23.0 °C | 600 Pa·s Show Supplier Material materials with Melt viscosity of 600 Pa·s | SABIC method |
Schrumpfung | 23.0 °C | 1.5 % Show Supplier Material materials with Schrumpfung of 1.5 % | SABIC method | 2.3-4.6 mm |
Schrumpfung, diagonal | 23.0 °C | 1 % Show Supplier Material materials with Schrumpfung, diagonal of 1 % | SABIC method | 0.75-2.3 mm |
Technological properties
Property | ||
---|---|---|
Availability | Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |