Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.46 g/cm³ Show Supplier Material materials with Dichte of 1.46 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 1.26 % Show Supplier Material materials with Moisture absorption of 1.26 % | ISO 62 | (23°C / 50% RH) |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 278 MPa Show Supplier Material materials with Biegefestigkeit of 278 MPa | ISO 178 |
Biegemodul | 23.0 °C | 9.5 GPa Show Supplier Material materials with Biegemodul of 9.5 GPa | ISO 178 |
Dehnung | 23.0 °C | 3.3 % Show Supplier Material materials with Dehnung of 3.3 % | ISO 527 | break |
Elastizitätsmodul | 23.0 °C | 13 GPa Show Supplier Material materials with Elastizitätsmodul of 13 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 133 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 133 J/m | ASTM D 256 | notched, 23°C |
Instrumented Impact, at Peak | 23.0 °C | 25 J Show Supplier Material materials with Instrumented Impact, at Peak of 25 J | ASTM D 3763 | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 17 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 17 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 92 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 92 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 186 MPa Show Supplier Material materials with Zugfestigkeit of 186 MPa | ISO 527 | break |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 208 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 208 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Relative temperature index, electrical | 130 °C Show Supplier Material materials with Relative temperature index, electrical of 130 °C | UL 746B | |
Relative temperature index, mechanical impact | 70 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 70 °C | UL 746B | |
Relative temperature index, mechanical strength | 85 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 85 °C | UL 746B | |
Wärmeformbeständigkeitstemperatur | 208 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 208 °C | ||
Entflammbarkeit | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101338758- - <br> UL Recognized, 94HB Flame Class Rating: 1.5mm UL 94 <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=103093423- - |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Heavy Vehicles | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 80°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |