Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of friction | 0.19 - 0.22 [-] Show Supplier Material materials with Coefficient of friction of 0.19 - 0.22 [-] | ||
Coefficient of friction, kinetic | 0.19 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.19 [-] | ASTM D 3702 Modified: Manual | |
Coefficient of friction, static | 0.22 [-] Show Supplier Material materials with Coefficient of friction, static of 0.22 [-] | ASTM D 3702 Modified: Manual | |
Dichte | 23.0 °C | 1.46 g/cm³ Show Supplier Material materials with Dichte of 1.46 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.1 % Show Supplier Material materials with Moisture absorption of 0.1 % | ISO 62 | (23°C / 50% RH) |
Relative Dichte | 23.0 °C | 1.46 [-] Show Supplier Material materials with Relative Dichte of 1.46 [-] | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.2 % Show Supplier Material materials with Wasserabsorption of 0.2 % | ISO 62-1 | (23°C/24hrs) |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 88 MPa Show Supplier Material materials with Biegefestigkeit of 88 MPa | ISO 178 | 2 mm/min |
Biegemodul | 23.0 °C | 3.3 GPa Show Supplier Material materials with Biegemodul of 3.3 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 5.9 % Show Supplier Material materials with Dehnung of 5.9 % | ISO 527 | yield, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 3.4 GPa Show Supplier Material materials with Elastizitätsmodul of 3.4 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 45 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 45 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 540 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 540 J/m | ASTM D 4812 | 23°C |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 14 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 14 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 9 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 40 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 40 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 62 MPa Show Supplier Material materials with Zugfestigkeit of 62 MPa | ISO 527 | yield, 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 152 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 152 °C | ISO 75/Cf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 104 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 104 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 7.7E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 7.7E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Vicat-Erweichungstemperatur | 153 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 153 °C | ISO 306 | Rate B/120 | |||
Wärmeformbeständigkeitstemperatur | 104 - 152 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 104 - 152 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.2E-4 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.2E-4 1/K | ISO 11359-2 | 23°C to 60°C | ||
Entflammbarkeit | UL Recognized, 94HB Flame Class Rating: ≥0.8mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101344678- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=102991912- - | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 13 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 13 g/10min | ASTM D1238 | 230°C/10 kgf | |
Schmelzvolumenflussrate | 11 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 11 cm³/10min | ISO 1133 | MVR at 230°C/10.0 kg | |
Schrumpfung | 23.0 °C | 1 % Show Supplier Material materials with Schrumpfung of 1 % | SABIC method |
Schrumpfung, diagonal | 23.0 °C | 1 % Show Supplier Material materials with Schrumpfung, diagonal of 1 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | ATM/Ticket Machine, Gear/Bearing/Slider, Industrial Material Handling, Irrigation | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Temperature: 80°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |