Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.44 g/cm³ Show Supplier Material materials with Dichte of 1.44 g/cm³ | ASTM D 792 |
Moisture absorption | 23.0 °C | 0.15 % Show Supplier Material materials with Moisture absorption of 0.15 % | ISO 62 | (23°C / 50% RH) |
Relative Dichte | 23.0 °C | 1.44 [-] Show Supplier Material materials with Relative Dichte of 1.44 [-] | ASTM D 792 | |
Specific volume | 23.0 °C | 0.7 cm³/g Show Supplier Material materials with Specific volume of 0.7 cm³/g | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.5 % Show Supplier Material materials with Wasserabsorption of 0.5 % | ISO 62-1 | (23°C/saturated) |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 154 MPa Show Supplier Material materials with Biegefestigkeit of 154 MPa | ISO 178 | yield, 2 mm/min |
Biegemodul | 23.0 °C | 7.8 GPa Show Supplier Material materials with Biegemodul of 7.8 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 3 % Show Supplier Material materials with Dehnung of 3 % | ISO 527 | yield, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 8.5 GPa Show Supplier Material materials with Elastizitätsmodul of 8.5 GPa | ISO 527 | 1 mm/min |
Hardness, Rockwell R | 23.0 °C | 109 [-] Show Supplier Material materials with Hardness, Rockwell R of 109 [-] | ASTM D 785 |
Impact strength, Izod notched, ASTM | 23.0 °C | 112 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 112 J/m | ASTM D 256 | notched, -30°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 640 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 640 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 17 J Show Supplier Material materials with Instrumented Impact, Total Energy of 17 J | ASTM D 3763 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 5 J Show Supplier Material materials with Instrumented Impact, at Peak of 5 J | ASTM D 3763 | 23°C |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 9 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 6 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 6 kJ/m² | ISO 180/1A | notched 80*10*4, -30°C |
Zugfestigkeit | 23.0 °C | 105 MPa Show Supplier Material materials with Zugfestigkeit of 105 MPa | ISO 527 | yield, 5 mm/min |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 204 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 204 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 155 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 155 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 2.7E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 2.7E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Relative temperature index, electrical | 140 °C Show Supplier Material materials with Relative temperature index, electrical of 140 °C | UL 746B | |||
Relative temperature index, mechanical impact | 130 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 130 °C | UL 746B | |||
Relative temperature index, mechanical strength | 140 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | |||
Vicat-Erweichungstemperatur | 150 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 150 °C | ISO 306 | Rate B/120 | |||
Wärmeformbeständigkeitstemperatur | 155 - 204 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 155 - 204 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.1E-4 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.1E-4 1/K | ISO 11359-2 | -40°C to 40°C | ||
Entflammbarkeit | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103956403- - <br> UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=103938404- - |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 4 [-] Show Supplier Material materials with Dielektrizitätskonstante, 1 MHz of 4 [-] | ASTM D 150 |
Dielektrizitätskonstante, 100 Hz | 23.0 °C | 4 [-] Show Supplier Material materials with Dielektrizitätskonstante, 100 Hz of 4 [-] | ASTM D 150 |
Dissipation factor, 100Hz | 23.0 °C | 3E-3 [-] Show Supplier Material materials with Dissipation factor, 100Hz of 3E-3 [-] | ASTM D 150 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 0.02 [-] | ASTM D 150 | |
Durchschlagfestigkeit | 23.0 °C | 27 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 27 kV/mm | IEC 60243-1 | in oil, 1.6 mm |
High Amp Arc Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm | ≥, UL 746A | PLC 3 |
High Volt Arc Track Rate | 23.0 °C | 1 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 1 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm | ≥, UL 746A | PLC 2 |
Kriechstromfestigkeit | 23.0 °C | 2 V Show Supplier Material materials with Kriechstromfestigkeit of 2 V | UL 746A | (UL) {PLC} |
Volume resistivity | 23.0 °C | 4.80E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 4.80E+15 Ω·cm | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 24 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 24 g/10min | ASTM D 1238 | 250°C/5.0 kgf | |
Schmelzvolumenflussrate | 19 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 19 cm³/10min | ISO 1133 | MVR at 265°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.3 % Show Supplier Material materials with Schrumpfung of 0.3 % | SABIC method | 0.75-2.3 mm |
Schrumpfung, diagonal | 23.0 °C | 0.7 % Show Supplier Material materials with Schrumpfung, diagonal of 0.7 % | SABIC method | 2.3-4.6 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Electronic Components | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 110°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |