Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Relative Dichte | 23.0 °C | 1.25 [-] Show Supplier Material materials with Relative Dichte of 1.25 [-] | ASTM D 792 | |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 145 MPa Show Supplier Material materials with Biegefestigkeit of 145 MPa | ISO 178 | break, 2 mm/min |
Biegemodul | 23.0 °C | 6.4 GPa Show Supplier Material materials with Biegemodul of 6.4 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 1.9 % Show Supplier Material materials with Dehnung of 1.9 % | ISO 527 | yield, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 7.5 GPa Show Supplier Material materials with Elastizitätsmodul of 7.5 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 37 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 37 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 347 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 347 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 82 J Show Supplier Material materials with Instrumented Impact, Total Energy of 82 J | ASTM D 3763 | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 4 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 4 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 21 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 21 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 95 MPa Show Supplier Material materials with Zugfestigkeit of 95 MPa | ISO 527 | yield, 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 97 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 97 °C | ASTM D 648 | 3.2 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 92 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 92 °C | ASTM D 648 | 3.2mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 2.6E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 2.6E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Relative temperature index, electrical | 60 °C Show Supplier Material materials with Relative temperature index, electrical of 60 °C | UL 746B | |||
Relative temperature index, mechanical impact | 60 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 60 °C | UL 746B | |||
Relative temperature index, mechanical strength | 60 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 60 °C | UL 746B | |||
Vicat-Erweichungstemperatur | 101 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 101 °C | ISO 306 | Rate B/120 | |||
Wärmeformbeständigkeitstemperatur | 92 - 97 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 92 - 97 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 7.4E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 7.4E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Entflammbarkeit | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221061- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=101632098- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥1mm UL 94 <br> UL Recognized, 94-5VB Flame Class Rating: ≥1.5mm UL 94 <br> Glow Wire Ignitability Temperature, 1.5 mm: 800°C IEC 60695-2-13 <br> Glow Wire Flammability Index, 1.5 mm: 960°C IEC 60695-2-12 | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
High Amp Arc Ignition | 23.0 °C | 1 mm Show Supplier Material materials with High Amp Arc Ignition of 1 mm | ≥, UL 746A | PLC 0 |
Hot-Wire Ignition | 23.0 °C | 1 mm Show Supplier Material materials with Hot-Wire Ignition of 1 mm | ≥, UL 746A | PLC 0 |
Sheet resistivity, ROA | 23.0 °C | 1000000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1000000 Ω | ASTM D 257 |
Volume resistivity | 23.0 °C | 1000 Ω·cm Show Supplier Material materials with Volume resistivity of 1000 Ω·cm | ASTM D 257 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 17 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 17 g/10min | ASTM D 1238 | 260°C/2.16 kgf | |
Schrumpfung | 23.0 °C | 0.1 % Show Supplier Material materials with Schrumpfung of 0.1 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.2 % Show Supplier Material materials with Schrumpfung, diagonal of 0.2 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Electronic Components, Wiring Devices, Vacuum Cleaner | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Temperature: 75 to 80.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |