Allgemein
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 127 MPa Show Supplier Material materials with Biegefestigkeit of 127 MPa | ISO 178 |
Biegemodul | 23.0 °C | 4.6 GPa Show Supplier Material materials with Biegemodul of 4.6 GPa | ISO 178 |
Dehnung | 23.0 °C | 3 % Show Supplier Material materials with Dehnung of 3 % | ISO 527 | break |
Elastizitätsmodul | 23.0 °C | 4.5 GPa Show Supplier Material materials with Elastizitätsmodul of 4.5 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 181 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 181 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 550 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 550 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 18 J Show Supplier Material materials with Instrumented Impact, at Peak of 18 J | ASTM D 3763 | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 9 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 38 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 38 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 74 MPa Show Supplier Material materials with Zugfestigkeit of 74 MPa | ISO 527 | break |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 146 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 146 °C | ASTM D 648 | 3.2 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 141 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 141 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 4.48E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 4.48E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Wärmeformbeständigkeitstemperatur | 141 - 146 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 141 - 146 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 4.99E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 4.99E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Entflammbarkeit | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101284270- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=101284354- - <br> UL Recognized, 94V-0 Flame Class Rating: 1.7mm UL 94 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Wearables, Aircraft Seating, Air Cabin Interiors, Document Handling, Electronic Components | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |