Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of friction | 0.17 [-] Show Supplier Material materials with Coefficient of friction of 0.17 [-] | ||
Coefficient of friction, kinetic | 0.17 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.17 [-] | ASTM D 3702 Modified: Manual | |
Dichte | 23.0 °C | 1.31 g/cm³ Show Supplier Material materials with Dichte of 1.31 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.05 % Show Supplier Material materials with Wasserabsorption of 0.05 % | ISO 62-1 | (23°C/saturated) |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 82 MPa Show Supplier Material materials with Biegefestigkeit of 82 MPa | ISO 178 |
Biegemodul | 23.0 °C | 2.2 GPa Show Supplier Material materials with Biegemodul of 2.2 GPa | ISO 178 |
Dehnung | 23.0 °C | 5.5 % Show Supplier Material materials with Dehnung of 5.5 % | ISO 527 | yield |
Elastizitätsmodul | 23.0 °C | 2.1 GPa Show Supplier Material materials with Elastizitätsmodul of 2.1 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 302 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 302 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 2000 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 2000 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 23 J Show Supplier Material materials with Instrumented Impact, at Peak of 23 J | ASTM D 3763 | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 19 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 19 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 129 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 129 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 50 MPa Show Supplier Material materials with Zugfestigkeit of 50 MPa | ISO 527 | yield |
Thermisch
| Property | Value | Comment | |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 127 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 127 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |
Wärmeformbeständigkeitstemperatur | 127 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 127 °C | ||
Entflammbarkeit | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101343864- - <br> UL Recognized, 94V-0 Flame Class Rating: 1.7mm UL 94 | ||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 18.1 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 18.1 g/10min | ASTM D 1238 | 300°C/2.16 kgf | |
Schrumpfung | 23.0 °C | 0.68 % Show Supplier Material materials with Schrumpfung of 0.68 % | SABIC method | 1.5-3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.67 % Show Supplier Material materials with Schrumpfung, diagonal of 0.67 % | SABIC method | 1.5-3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | ATM/Ticket Machine | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Temperature: 120°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |