Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1 g/cm³ Show Supplier Material materials with Dichte of 1 g/cm³ | ISO 1183 |
Mechanisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Biegefestigkeit | 23.0 °C | 40 MPa Show Supplier Material materials with Biegefestigkeit of 40 MPa | ISO 178 | break, 2 mm/min | ||
Biegemodul | 23.0 °C | 1.6 GPa Show Supplier Material materials with Biegemodul of 1.6 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 4.3 % Show Supplier Material materials with Dehnung of 4.3 % | ISO 527 | yield, 5 mm/min | ||
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 60 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 60 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C | ||
Zugfestigkeit | 23.0 °C | 16 MPa Show Supplier Material materials with Zugfestigkeit of 16 MPa | ISO 527 | break, 5 mm/min | ||
Schlagzähigkeit, Izod ungekerbt | ISO 180/1U | 80*10*4, 23°C |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 110 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 110 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 61 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 61 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.3E-4 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.3E-4 1/K | ISO 11359-2 | 23°C to 60°C | ||
Relative temperature index, electrical | 65 °C Show Supplier Material materials with Relative temperature index, electrical of 65 °C | UL 746B | |||
Relative temperature index, mechanical impact | 65 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | |||
Relative temperature index, mechanical strength | 65 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | |||
Wärmeformbeständigkeitstemperatur | 61 - 110 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 61 - 110 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.48E-4 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.48E-4 1/K | ISO 11359-2 | 23°C to 60°C | ||
Entflammbarkeit | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101282741- - <br> UL Recognized, 94HB Flame Class Rating: 1.5mm UL 94 |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 100 - 10000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 100 - 10000 Ω | ASTM D 257 |
Rheological Properties
Property | Value | Comment |
---|---|---|
Schmelzvolumenflussrate | 10 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 10 cm³/10min | ISO 1133 | MVR at 240°C/5.0 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Wireless Communications, Document Handling, Conveyor | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 80°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |