Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.635 g/cm³ Show Supplier Material materials with Dichte of 1.635 g/cm³ | ASTM D 792 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 223 MPa Show Supplier Material materials with Biegefestigkeit of 223 MPa | ASTM D 790 | brk, 1.3 mm/min, 50 mm span |
Biegemodul | 23.0 °C | 13.8 GPa Show Supplier Material materials with Biegemodul of 13.8 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Dehnung | 23.0 °C | 1.9 % Show Supplier Material materials with Dehnung of 1.9 % | ISO 527 | break, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 15.1 GPa Show Supplier Material materials with Elastizitätsmodul of 15.1 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 127 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 127 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 520 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 520 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 21 J Show Supplier Material materials with Instrumented Impact, at Peak of 21 J | ASTM D 3763 | 23°C |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 12 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 12 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 127 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 127 kJ/m² | ASTM D 256 | notched, 23°C |
Zugfestigkeit | 23.0 °C | 153 MPa Show Supplier Material materials with Zugfestigkeit of 153 MPa | ISO 527 | break, 5 mm/min |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 107 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 107 °C | ASTM D 648 | 3.2mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.39E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.39E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Wärmeformbeständigkeitstemperatur | 107 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 107 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 4.15E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 4.15E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Entflammbarkeit | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101219669- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥1mm UL 94 <br> UL Recognized, 94V-1 Flame Class Rating: ≥0.8mm UL 94 |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 5.00E+16 Ω Show Supplier Material materials with Sheet resistivity, ROA of 5.00E+16 Ω | ASTM D 257 |
Volume resistivity | 23.0 °C | 2.15E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 2.15E+16 Ω·cm | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 48.6 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 48.6 g/10min | ASTM D 1238 | 300°C/5.0 kgf | |
Schmelzvolumenflussrate | 17 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 17 cm³/10min | ASTM D 1238 | MVR at 300°C/2.16 kg | |
Schrumpfung | 23.0 °C | 0.05 % Show Supplier Material materials with Schrumpfung of 0.05 % | ASTM D 955 | 24 hrs |
Schrumpfung, diagonal | 23.0 °C | 0.05 % Show Supplier Material materials with Schrumpfung, diagonal of 0.05 % | ASTM D 955 | 24 hrs |
Technological properties
Property | ||
---|---|---|
Application areas | Personal Computing, Wireless Communications, Electronic Components, Heavy Vehicles, Data Transfer | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 110°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |