Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.35 g/cm³ Show Supplier Material materials with Dichte of 1.35 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 0.03 % Show Supplier Material materials with Wasserabsorption of 0.03 % | ISO 62-1 | (23°C/24hrs) |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 95 MPa Show Supplier Material materials with Biegefestigkeit of 95 MPa | ISO 178 | yield, 2 mm/min |
Biegemodul | 23.0 °C | 2.6 GPa Show Supplier Material materials with Biegemodul of 2.6 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 16 % Show Supplier Material materials with Dehnung of 16 % | ISO 527 | break, 50 mm/min |
Elastizitätsmodul | 23.0 °C | 2.5 GPa Show Supplier Material materials with Elastizitätsmodul of 2.5 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 280 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 280 J/m | ASTM D 256 | notched, 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 30 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 30 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 56 MPa Show Supplier Material materials with Zugfestigkeit of 56 MPa | ISO 527 | yield, 50 mm/min |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 173 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 173 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 155 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 155 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 6.1E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 6.1E-5 1/K | ASTM E 831 | -40°C to 150°C | ||
Relative temperature index, electrical | 65 °C Show Supplier Material materials with Relative temperature index, electrical of 65 °C | UL 746B | |||
Relative temperature index, mechanical impact | 65 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | |||
Relative temperature index, mechanical strength | 65 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | |||
Wärmeformbeständigkeitstemperatur | 155 - 173 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 155 - 173 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 8.7E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 8.7E-5 1/K | ASTM E 831 | -40°C to 150°C | ||
Entflammbarkeit | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=102719345- - <br> UL Recognized, 94HB Flame Class Rating: 1mm UL 94 |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 10GHz | 23.0 °C | 3.58 [-] Show Supplier Material materials with Dielectric constant, 10GHz of 3.58 [-] | SABIC method |
Dielectric constant, 1GHz | 23.0 °C | 3.56 [-] Show Supplier Material materials with Dielectric constant, 1GHz of 3.56 [-] | SABIC method | 1.1 GHz |
Dielectric constant, 5GHz | 23.0 °C | 3.57 [-] Show Supplier Material materials with Dielectric constant, 5GHz of 3.57 [-] | SABIC method |
Dielektrizitätskonstante | 23.0 °C | 3.57 [-] Show Supplier Material materials with Dielektrizitätskonstante of 3.57 [-] | SABIC method | 1.9 GHz |
Dissipation factor, 1GHz | 23.0 °C | 9E-4 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 9E-4 [-] | SABIC method | |
Dissipation factor, 5GHz | 23.0 °C | 1.9E-3 [-] Show Supplier Material materials with Dissipation factor, 5GHz of 1.9E-3 [-] | SABIC method |
Verlustfaktor | 23.0 °C | 1.1E-3 [-] Show Supplier Material materials with Verlustfaktor of 1.1E-3 [-] | SABIC method |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 36 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 36 g/10min | ASTM D 1238 | 300°C/10 kgf | |
Schmelzvolumenflussrate | 9 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 9 cm³/10min | ISO 1133 | MVR at 300°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.6 % Show Supplier Material materials with Schrumpfung of 0.6 % | ISO 294 | 24 hrs |
Schrumpfung, diagonal | 23.0 °C | 0.6 % Show Supplier Material materials with Schrumpfung, diagonal of 0.6 % | ISO 294 | 24 hrs |
Technological properties
Property | ||
---|---|---|
Application areas | Wireless Communications | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 105°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |