Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.03 g/cm³ Show Supplier Material materials with Dichte of 1.03 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.03 % Show Supplier Material materials with Moisture absorption of 0.03 % | ASTM D 570 | (23°C/50% RH/24 hrs) |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 104 MPa Show Supplier Material materials with Biegefestigkeit of 104 MPa | ISO 178 |
Biegemodul | 23.0 °C | 5.6 GPa Show Supplier Material materials with Biegemodul of 5.6 GPa | ISO 178 |
Dehnung | 23.0 °C | 2.2 % Show Supplier Material materials with Dehnung of 2.2 % | ISO 527 | break |
Elastizitätsmodul | 23.0 °C | 5.1 GPa Show Supplier Material materials with Elastizitätsmodul of 5.1 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 48 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 48 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 325 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 325 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 8 J Show Supplier Material materials with Instrumented Impact, at Peak of 8 J | ASTM D 3763 | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 5 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 20 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 20 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 65 MPa Show Supplier Material materials with Zugfestigkeit of 65 MPa | ISO 527 | break |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 160 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 160 °C | ASTM D 648 | 3.2 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 145 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 145 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 105 °C Show Supplier Material materials with Relative temperature index, electrical of 105 °C | UL 746B | |||
Relative temperature index, mechanical impact | 105 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | |||
Relative temperature index, mechanical strength | 105 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C | UL 746B | |||
Wärmeformbeständigkeitstemperatur | 145 - 160 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 145 - 160 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 7.45E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 7.45E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Entflammbarkeit | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101284109- - <br> UL Recognized, 94HB Flame Class Rating: ≥0.75mm UL 94 | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
High Amp Arc Ignition | 23.0 °C | 0.75 mm Show Supplier Material materials with High Amp Arc Ignition of 0.75 mm | ≥, UL 746A | PLC 0 |
High Volt Arc Track Rate | 23.0 °C | 0 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 0 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 0.75 mm Show Supplier Material materials with Hot-Wire Ignition of 0.75 mm | ≥, UL 746A | PLC 4 |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Application areas | Pharmaceutical Manufacturing | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Temperature: 80°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |