Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.05 g/cm³ Show Supplier Material materials with Dichte of 1.05 g/cm³ | ISO 1183 |
Relative Dichte | 23.0 °C | 1.05 [-] Show Supplier Material materials with Relative Dichte of 1.05 [-] | ASTM D 792 | |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 76 MPa Show Supplier Material materials with Biegefestigkeit of 76 MPa | ISO 178 | yield, 2 mm/min |
Biegemodul | 23.0 °C | 2.4 GPa Show Supplier Material materials with Biegemodul of 2.4 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 24.8 % Show Supplier Material materials with Dehnung of 24.8 % | ISO 527 | break, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 2.5 GPa Show Supplier Material materials with Elastizitätsmodul of 2.5 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 133 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 133 J/m | ASTM D 256 |
Instrumented Impact, Total Energy | 23.0 °C | 30 J Show Supplier Material materials with Instrumented Impact, Total Energy of 30 J | ASTM D 3763 | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 8 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 8 kJ/m² | ISO 180/1A | notched 80*10*4, -30°C |
Zugfestigkeit | 23.0 °C | 35 MPa Show Supplier Material materials with Zugfestigkeit of 35 MPa | ISO 527 | break, 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 94 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 94 °C | ASTM D 648 | 3.2 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 80 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 80 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 8.82E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 8.82E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Relative temperature index, electrical | 65 °C Show Supplier Material materials with Relative temperature index, electrical of 65 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 65 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | |||
Vicat-Erweichungstemperatur | 100 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 100 °C | ISO 306 | Rate B/50 | |||
Wärmeformbeständigkeitstemperatur | 80 - 94 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 80 - 94 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 8.82E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 8.82E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Entflammbarkeit | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103956405- - <br> UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
High Amp Arc Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm | ≥, UL 746A | PLC 0 |
High Volt Arc Track Rate | 23.0 °C | 3 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 3 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm | ≥, UL 746A | PLC 4 |
Kriechstromfestigkeit | 23.0 °C | 0 V Show Supplier Material materials with Kriechstromfestigkeit of 0 V | UL 746A | (UL) {PLC} |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 19 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 19 g/10min | ISO 1133 | 220°C/10.0 kg | |
Schrumpfung | 23.0 °C | 0.5 % Show Supplier Material materials with Schrumpfung of 0.5 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Others, Medical Device, Pharmaceutical Packaging & Drug Delivery, Surgical Devices | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Temperature: 80 to 95.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |