Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of friction | 0.33 - 0.62 [-] Show Supplier Material materials with Coefficient of friction of 0.33 - 0.62 [-] | ||
Coefficient of friction, kinetic | 0.33 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.33 [-] | ASTM D 3702 Modified: Instr. | |
Coefficient of friction, static | 0.62 [-] Show Supplier Material materials with Coefficient of friction, static of 0.62 [-] | ASTM D 3702 Modified: Instr. | |
Dichte | 23.0 °C | 1.42 g/cm³ Show Supplier Material materials with Dichte of 1.42 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 0.4 % Show Supplier Material materials with Wasserabsorption of 0.4 % | ISO 62-1 | (23°C/24hrs) |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 340 MPa Show Supplier Material materials with Biegefestigkeit of 340 MPa | ISO 178 | yield, 2 mm/min |
Biegemodul | 23.0 °C | 19.9 GPa Show Supplier Material materials with Biegemodul of 19.9 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 1.3 % Show Supplier Material materials with Dehnung of 1.3 % | ISO 527 | break, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 25.1 GPa Show Supplier Material materials with Elastizitätsmodul of 25.1 GPa | ISO 527 | 1 mm/min |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 7 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 7 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 40 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 40 kJ/m² | ISO 180/1U | unnotched 80*10*4 |
Zugfestigkeit | 23.0 °C | 256 MPa Show Supplier Material materials with Zugfestigkeit of 256 MPa | ISO 527 | break, 5 mm/min |
Thermisch
Property | Temperature | Value | Comment |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 270 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 270 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 8E-6 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 8E-6 1/K | ISO 11359-2 | 23°C to 60°C |
Wärmeformbeständigkeitstemperatur | 270 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 270 °C | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 5.1E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 5.1E-5 1/K | ISO 11359-2 | 23°C to 60°C |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 10 - 1000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 10 - 1000 Ω | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schrumpfung | 23.0 °C | 0.05 % Show Supplier Material materials with Schrumpfung of 0.05 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Sensor, Heavy Vehicles, Gear/Bearing/Slider, Lawn/Garden, EV Infrastructure, Electronic Components, Auto Aftermarket | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120 to 150.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |