FLEX NORYL™ Resin WCD815U - Asia

Want to keep this datasheet? Save it now in your required format

Description

FLEX NORYL™ WCD815U resin is a flexible, non-reinforced extrudable blend of Polyphenylene Ether (PPE) + Thermoplastic Elastomer (TPE). This UV stabilized material contains non-halogenated flame retardant and performance capable of meeting UL 1581 VW-1 requirements. FLEX NORYL WCD815U resin is intended for evaluation in AC cable jacket applications that require UL62 at 90C temperature rating and light color. It has a Shore A Hardness reading of 81 and exhibits superior thermal stability, very low water absorption, good electric properties, and low specific gravity. Processing is typically conducted on standard extrusion equipment, and UL 1581 testing is conducted on 2.0mm wire with 0.12mm X 20 stranded copper conductor.

Diese Materialdaten wurden von Sabic zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Anwendungen

Elektrotechnik

Elektronik

Anzeigegeräte

Materialien von diesem Anbieter

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

Sehen Sie alle Materialen dieses Anbieters

Eigenschaften

Allgemein

Property	Temperature	Value	Comment
Relative Dichte	23.0 °C	1.03 [-] Show Supplier Material materials with Relative Dichte of 1.03 [-]	ASTM D 792 \|
Sauerstoffindex	23.0 °C	27 % Show Supplier Material materials with Sauerstoffindex of 27 %

Mechanisch

Property	Temperature	Value	Comment
Biegemodul	23.0 °C	0 GPa Show Supplier Material materials with Biegemodul of 0 GPa	ISO 178 \| 12.5 mm/min
Dehnung	23.0 °C	260 % Show Supplier Material materials with Dehnung of 260 %	ISO 527 \| break, 50 mm/min
Härte, Shore A	23.0 °C	81 [-] Show Supplier Material materials with Härte, Shore A of 81 [-]	ASTM D 2240 \| 30S reading
Zugfestigkeit	23.0 °C	17 MPa Show Supplier Material materials with Zugfestigkeit of 17 MPa	ISO 527 \| break, 50 mm/min

Thermisch

Property	Value	Comment
Glow Wire Ignition Temperature	775 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 775 °C	IEC 60695-2-13 \| 3.0 mm
Entflammbarkeit	Smoke Density on 0.5mm plaque, Flame, Ds, max: 117- ASTM E 662 <br> Smoke Density on 0.5mm plaque, Non-flame, Ds, max: 166- ASTM E 662 <br> Glow Wire Flammability Index 850°C, passes at: 3mm IEC 60695-2-12

Elektrisch

Property	Temperature	Value	Comment
Dielectric constant, 5GHz	23.0 °C	2.6 [-] Show Supplier Material materials with Dielectric constant, 5GHz of 2.6 [-]	SABIC method
Dissipation factor, 5GHz	23.0 °C	2E-3 [-] Show Supplier Material materials with Dissipation factor, 5GHz of 2E-3 [-]	SABIC method
Durchschlagfestigkeit	23.0 °C	25 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 25 kV/mm	ASTM D 149 \| in oil
Kriechstromfestigkeit	23.0 °C	600 V Show Supplier Material materials with Kriechstromfestigkeit of 600 V	IEC 60112 \|
Sheet resistivity, ROA	23.0 °C	1.60E+16 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.60E+16 Ω	ASTM D 257
Volume resistivity	23.0 °C	5.10E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 5.10E+15 Ω·cm	ASTM D 257

Rheological Properties

Property	Value	Comment
Schmelzmassenflussrate	10 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 10 g/10min	ASTM D 1238 \| 250°C/10.0 kgf

Technological properties

Property
Application areas	Wire & cable
Availability	Asia,Americas
Processing methods	Head Zone Temperature: 220 to 250.0°C Die Temperature: 220 to 250.0°C Water Bath Temperature: 15 to 60.0°C Conductor Pre-heat Temperature: 25 to 120.0°C Drying Time: 5 to 7.0hrs Maximum Moisture Content: 0.02% Neck Temperature: 220 to 250.0°C Drying Time (Cumulative): 12hrs Screen Pack: 150 to 100.0- Screw Speed: 15 to 85.0rpm Cross-head Temperature: 220 to 250.0°C Middle Zone Temperatures: 220 to 250.0°C Cooling Water Air Gap: 100 to 200.0mm Drying Temperature: 75 to 85.0°C Melt Temperature: 220 to 250.0°C Feed Zone Temperature: 180 to 220.0°C Extruder Length/Diameter Ratio (L/D): 22:1 to 26:1-
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.