Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.3 g/cm³ Show Supplier Material materials with Dichte of 1.3 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.06 % Show Supplier Material materials with Moisture absorption of 0.06 % | ISO 62 | (23°C / 50% RH) |
Wasserabsorption | 23.0 °C | 0.2 % Show Supplier Material materials with Wasserabsorption of 0.2 % | ISO 62-1 | (23°C/saturated) |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 192 MPa Show Supplier Material materials with Biegefestigkeit of 192 MPa | ISO 178 | break, 2 mm/min |
Biegemodul | 23.0 °C | 8.1 GPa Show Supplier Material materials with Biegemodul of 8.1 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 2.5 % Show Supplier Material materials with Dehnung of 2.5 % | ISO 527 | break, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 9.6 GPa Show Supplier Material materials with Elastizitätsmodul of 9.6 GPa | ISO 527 | 1 mm/min |
Hardness, Ball Indentation | 23.0 °C | 240 MPa Show Supplier Material materials with Hardness, Ball Indentation of 240 MPa | ISO 2039-1 | H358/30 |
Impact strength, Izod notched, ASTM | 23.0 °C | 85 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 85 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 465 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 465 J/m | ASTM D 4812 | unnotched, -30°C |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 30 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 30 kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 8 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 8 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 30 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 30 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Taber Abrasion | 23.0 °C | 65 mg/1000cy Show Supplier Material materials with Taber Abrasion of 65 mg/1000cy | SABIC method | CS-17, 1 kg |
Zugfestigkeit | 23.0 °C | 133 MPa Show Supplier Material materials with Zugfestigkeit of 133 MPa | ISO 527 | break, 5 mm/min |
Thermisch
Property | Temperature | Value | Comment |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 150 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 150 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |
Heat deflection temperature, 1.80 MPa | 145 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 145 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 3E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 3E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Vicat-Erweichungstemperatur | 158 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 158 °C | ISO 306 | Rate B/120 | |
Wärmeformbeständigkeitstemperatur | 145 - 150 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 145 - 150 °C | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 7E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 7E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 9 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 9 g/10min | ASTM D 1238 | 300°C/5.0 kgf | |
Schmelzvolumenflussrate | 30 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 30 cm³/10min | ISO 1133 | MVR at 300°C/10.0 kg | |
Schrumpfung | 23.0 °C | 0.1 % Show Supplier Material materials with Schrumpfung of 0.1 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.2 % Show Supplier Material materials with Schrumpfung, diagonal of 0.2 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Vending Machine, Water Treatment/Filtration, Meter Water, Smart Water Meter, Small Appliance, Plumbing, Pipe/Fitting, Pump, Heavy Vehicles, Hot Water System, Fixture Bath/Shower, Electronic Components, Coffee Maker/Espresso Machine | |
Availability | Europe,Asia,MEA,Americas | |
Processing methods | Hopper Temperature: 60 to 80.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |