Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Moisture absorption | 23.0 °C | 1.19 % Show Supplier Material materials with Moisture absorption of 1.19 % | ASTM D 570 | (50% RH, Equilibrium) |
Relative Dichte | 23.0 °C | 1.08 [-] Show Supplier Material materials with Relative Dichte of 1.08 [-] | ASTM D 792 | |
Wasserabsorption | 23.0 °C | 3.5 % Show Supplier Material materials with Wasserabsorption of 3.5 % | ASTM D 570 | (23°C/Saturated) |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 70 MPa Show Supplier Material materials with Biegefestigkeit of 70 MPa | ISO 178 | yield, 2 mm/min |
Biegemodul | 23.0 °C | 1.8 GPa Show Supplier Material materials with Biegemodul of 1.8 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 4 % Show Supplier Material materials with Dehnung of 4 % | ISO 527 | yield, 50 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 528 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 528 J/m | ASTM D 256 |
Instrumented Impact, Total Energy | 23.0 °C | 41 J Show Supplier Material materials with Instrumented Impact, Total Energy of 41 J | ASTM D 3763 | 23°C |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 20 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 20 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, -30°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 50 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 50 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 50 MPa Show Supplier Material materials with Zugfestigkeit of 50 MPa | ISO 527 | yield, 50 mm/min |
Thermisch
Property | Temperature | Value | Comment |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 175 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 175 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |
Vicat-Erweichungstemperatur | 240 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 240 °C | ISO 306 | Rate A/50 | |
Wärmeformbeständigkeitstemperatur | 175 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 175 °C | ||
Wärmeleitfähigkeit | 23.0 °C | 0.23 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 0.23 W/(m·K) | ASTM C177 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzvolumenflussrate | 7 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 7 cm³/10min | ISO 1133 | MVR at 280°C/2.16 kg | |
Schrumpfung | 23.0 °C | 1.5 % Show Supplier Material materials with Schrumpfung of 1.5 % | SABIC method |
Schrumpfung, diagonal | 23.0 °C | 1.3 % Show Supplier Material materials with Schrumpfung, diagonal of 1.3 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Bumper, Interior, Thin wall packaging | |
Availability | Europe,Asia,Americas | |
Processing methods | Maximum Moisture Content: 0.07% | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |