Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.29 g/cm³ Show Supplier Material materials with Dichte of 1.29 g/cm³ | ASTM D 792 |
Moisture absorption | 23.0 °C | 0.23 % Show Supplier Material materials with Moisture absorption of 0.23 % | ISO 62 | (23°C / 50% RH) |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 102 MPa Show Supplier Material materials with Biegefestigkeit of 102 MPa | ISO 178 |
Biegemodul | 23.0 °C | 3 GPa Show Supplier Material materials with Biegemodul of 3 GPa | ISO 178 |
Dehnung | 23.0 °C | 4.6 % Show Supplier Material materials with Dehnung of 4.6 % | ISO 527 | yield |
Elastizitätsmodul | 23.0 °C | 2.7 GPa Show Supplier Material materials with Elastizitätsmodul of 2.7 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 279 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 279 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 2160 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 2160 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 37 J Show Supplier Material materials with Instrumented Impact, at Peak of 37 J | ASTM D 3763 | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 9 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 134 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 134 kJ/m² | ISO 180/1U | unnotched 80*10*4 |
Zugfestigkeit | 23.0 °C | 55 MPa Show Supplier Material materials with Zugfestigkeit of 55 MPa | ISO 527 | yield |
Thermisch
Property | Value | Comment |
---|---|---|
Heat deflection temperature, 0.45 MPa | 140 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 140 °C | ASTM D 648 | 3.2 mm, unannealed |
Heat deflection temperature, 1.80 MPa | 126 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 126 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
Wärmeformbeständigkeitstemperatur | 126 - 140 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 126 - 140 °C |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 100 Ω Show Supplier Material materials with Sheet resistivity, ROA of 100 Ω | ASTM D 257 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Data Management, Document Handling, Enclosures, Electronic Components, Infotainment/Telematic, Personal Computing | |
Availability | Europe,Asia,Americas | |
Processing methods | Front - Zone 3 Temperature: 320 to 330.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |