Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.275 g/cm³ Show Supplier Material materials with Dichte of 1.275 g/cm³ | ASTM D 792 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegemodul | 23.0 °C | 2.6 GPa Show Supplier Material materials with Biegemodul of 2.6 GPa | ASTM D 790 | 1.3 mm/min |
Dehnung | 23.0 °C | 2.3 % Show Supplier Material materials with Dehnung of 2.3 % | ASTM D638 | brk, Type I, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 2.2 GPa Show Supplier Material materials with Elastizitätsmodul of 2.2 GPa | ASTM D638 |
Impact strength, Izod notched, ASTM | 23.0 °C | 104 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 104 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 1003 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 1003 J/m | ASTM D 256 | un-notched, 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 33 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 33 kJ/m² | ASTM D 256 | notched, 23°C |
Zugfestigkeit | 23.0 °C | 45 MPa Show Supplier Material materials with Zugfestigkeit of 45 MPa | ASTM D638 | brk, Type I, 5 mm/min |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 175 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 175 °C | ASTM D648 | 3.2 mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 6.21E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 6.21E-5 1/K | ASTM E 831 | ||
Wärmeformbeständigkeitstemperatur | 175 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 175 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 61.1 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 61.1 1/K | ASTM E 831 | ||
Entflammbarkeit | Vertical Burn a (60s) passes at: 0sec FAR 25.853 <br> Vertical Burn b (12s) passes at: 0sec FAR 25.853 <br> FAA Flammability: PASS- FAR 25.853 <br> OSU total heat release (2 minute test): 44kW-min/m² FAR 25.853 <br> OSU peak heat release rate (5 minute test): 45kW/m² FAR 25.853 |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 100MHz | 23.0 °C | 2.71 [-] Show Supplier Material materials with Dielectric constant, 100MHz of 2.71 [-] | ASTM D 150 |
Dielectric constant, 500MHz | 23.0 °C | 2.53 [-] Show Supplier Material materials with Dielectric constant, 500MHz of 2.53 [-] | ASTM D 150 |
Dissipation factor, 100MHz | 23.0 °C | 3E-3 [-] Show Supplier Material materials with Dissipation factor, 100MHz of 3E-3 [-] | ASTM D 150 |
Dissipation factor, 1GHz | 23.0 °C | 4E-3 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 4E-3 [-] | ASTM D 150 |
Dissipation factor, 500MHz | 23.0 °C | 5.67E-3 [-] Show Supplier Material materials with Dissipation factor, 500MHz of 5.67E-3 [-] | ASTM D 150 |
Volume resistivity | 23.0 °C | 1.10E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.10E+15 Ω·cm | ASTM D 257 |
Technological properties
Property | ||
---|---|---|
Application areas | Fused Deposition Modeling (FDM), Additive Plastic | |
Availability | Europe,Americas | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |