Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.45 g/cm³ Show Supplier Material materials with Dichte of 1.45 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.1 % Show Supplier Material materials with Moisture absorption of 0.1 % | ISO 62 | (23°C / 50% RH) |
Relative Dichte | 23.0 °C | 1.45 [-] Show Supplier Material materials with Relative Dichte of 1.45 [-] | ASTM D 792 | |
Wasserabsorption | 23.0 °C | 0.3 % Show Supplier Material materials with Wasserabsorption of 0.3 % | ASTM D 570 | (23°C/Saturated) |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 280 MPa Show Supplier Material materials with Biegefestigkeit of 280 MPa | ISO 178 | yield, 2 mm/min |
Biegemodul | 23.0 °C | 12.3 GPa Show Supplier Material materials with Biegemodul of 12.3 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 2 % Show Supplier Material materials with Dehnung of 2 % | ISO 527 | break, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 13.9 GPa Show Supplier Material materials with Elastizitätsmodul of 13.9 GPa | ISO 527 | 1 mm/min |
Hardness, Rockwell R | 23.0 °C | 108 [-] Show Supplier Material materials with Hardness, Rockwell R of 108 [-] | ASTM D 785 |
Impact strength, Izod notched, ASTM | 23.0 °C | 90 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 90 J/m | ASTM D 256 |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 11 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 11 kJ/m² | ISO 179/2C | -30°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 11 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 11 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 198 MPa Show Supplier Material materials with Zugfestigkeit of 198 MPa | ISO 527 | break, 5 mm/min |
Thermisch
Property | Temperature | Value | Comment |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 258 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 258 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 244 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 244 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.6E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.6E-5 1/K | ASTM E 831 | -40°C to 40°C |
Vicat-Erweichungstemperatur | 246 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 246 °C | ISO 306 | Rate B/50 | |
Wärmeformbeständigkeitstemperatur | 244 - 258 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 244 - 258 °C | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 9E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 9E-5 1/K | ASTM E 831 | -40°C to 40°C |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzvolumenflussrate | 10 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 10 cm³/10min | ISO 1133 | MVR at 220°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.24 % Show Supplier Material materials with Schrumpfung of 0.24 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.6 % Show Supplier Material materials with Schrumpfung, diagonal of 0.6 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | EV Infrastructure, Electronic Components, Transmission/Transfer Comp, Personal Computing | |
Availability | Europe,Asia,Americas | |
Processing methods | Minimum Moisture Content: 0.02% | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |