Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.107 g/cm³ Show Supplier Material materials with Dichte of 1.107 g/cm³ | ASTM D 792 |
Moisture absorption | 23.0 °C | 1 % Show Supplier Material materials with Moisture absorption of 1 % | ASTM D 570 | (50% RH, Equilibrium) |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 95 MPa Show Supplier Material materials with Biegefestigkeit of 95 MPa | ASTM D 790 | yld, 2.6 mm/min, 100 mm span |
Biegemodul | 23.0 °C | 2.2 GPa Show Supplier Material materials with Biegemodul of 2.2 GPa | ASTM D 790 | 2.6 mm/min, 100 mm span |
Dehnung | 23.0 °C | 60 % Show Supplier Material materials with Dehnung of 60 % | ASTM D 638 | brk, Type I, 50 mm/min |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 240 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 240 kJ/m² | ASTM D 256 | notched, 23°C |
Zugfestigkeit | 23.0 °C | 59 MPa Show Supplier Material materials with Zugfestigkeit of 59 MPa | ASTM D 638 | yld, Type I, 50 mm/min |
Thermisch
Property | Temperature | Value | Comment |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 193 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 193 °C | ASTM D 648 | 6.4 mm, unannealed | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.26E-4 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.26E-4 1/K | ASTM E 831 | 60°C to 138°C |
Vicat-Erweichungstemperatur | 232 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 232 °C | ASTM D 1525 | Rate B/50 | |
Wärmeformbeständigkeitstemperatur | 193 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 193 °C | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.26E-4 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.26E-4 1/K | ASTM E 831 | 60°C to 138°C |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schrumpfung | 23.0 °C | 1.1 % Show Supplier Material materials with Schrumpfung of 1.1 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Heavy Vehicles, Head Protection, Energy Absorber, Door Handle, Document Handling, Console, Cladding, Auto Aftermarket, Pump, Small Appliance, Medical Device, Wheel Cover | |
Availability | Europe,Asia,Americas | |
Processing methods | Rear - Zone 1 Temperature: 265 to 305.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |