Eigenschaften
Allgemein
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 169 MPa Show Supplier Material materials with Biegefestigkeit of 169 MPa | ASTM D 790 | yld, 1.3 mm/min, 50 mm span |
Biegemodul | 23.0 °C | 8.1 GPa Show Supplier Material materials with Biegemodul of 8.1 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Dehnung | 23.0 °C | 1.8 % Show Supplier Material materials with Dehnung of 1.8 % | ASTM D 638 | brk, Type I, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 10.1 GPa Show Supplier Material materials with Elastizitätsmodul of 10.1 GPa | ASTM D 638 | 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 76 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 76 J/m | ASTM D 256 | notched, 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 76 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 76 kJ/m² | ASTM D 256 | notched, 23°C |
Zugfestigkeit | 23.0 °C | 148 MPa Show Supplier Material materials with Zugfestigkeit of 148 MPa | ASTM D 638 | brk, Type I, 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 203 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 203 °C | ASTM D 648 | 3.2mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.43E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.43E-5 1/K | ASTM E 831 | -40°C to 150°C | ||
Relative temperature index, electrical | 105 °C Show Supplier Material materials with Relative temperature index, electrical of 105 °C | UL 746B | |||
Relative temperature index, mechanical impact | 105 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | |||
Relative temperature index, mechanical strength | 105 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C | UL 746B | |||
Wärmeformbeständigkeitstemperatur | 203 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 203 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 5.5E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 5.5E-5 1/K | ASTM E 831 | -40°C to 150°C | ||
Entflammbarkeit | UL Recognized, 94V-0 Flame Class Rating: 1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=102158299- - | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 15.4 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 15.4 g/10min | ASTM D 1238 | 337°C/6.6 kgf | |
Schmelzvolumenflussrate | 34 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 34 cm³/10min | ISO 1133 | MVR at 345°C/10.0 kg | |
Schrumpfung | 23.0 °C | 0.3 % Show Supplier Material materials with Schrumpfung of 0.3 % | SABIC method |
Schrumpfung, diagonal | 23.0 °C | 0.53 % Show Supplier Material materials with Schrumpfung, diagonal of 0.53 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Semiconductor | |
| Availability | Asia | |
| Processing methods | Melt Temperature: 350 to 400.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |