Eigenschaften
Allgemein
| Property | Temperature | Value |
|---|---|---|
Sauerstoffindex | 23.0 °C | 48 % Show Supplier Material materials with Sauerstoffindex of 48 % |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 150 MPa Show Supplier Material materials with Biegefestigkeit of 150 MPa | ISO 178 | yield, 2 mm/min |
Biegemodul | 23.0 °C | 3.8 GPa Show Supplier Material materials with Biegemodul of 3.8 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 7 % Show Supplier Material materials with Dehnung of 7 % | ISO 527 | break, 5 mm/min |
Taber Abrasion | 23.0 °C | 35 mg/1000cy Show Supplier Material materials with Taber Abrasion of 35 mg/1000cy | SABIC method | CS-17, 1 kg |
Zugfestigkeit | 23.0 °C | 90 MPa Show Supplier Material materials with Zugfestigkeit of 90 MPa | ISO 527 | break, 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 202 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 202 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 4.5E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 4.5E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Relative temperature index, electrical | 105 °C Show Supplier Material materials with Relative temperature index, electrical of 105 °C | UL 746B | |||
Relative temperature index, mechanical impact | 105 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | |||
Relative temperature index, mechanical strength | 105 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C | UL 746B | |||
Vicat-Erweichungstemperatur | 222 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 222 °C | ISO 306 | Rate B/50 | |||
Wärmeformbeständigkeitstemperatur | 202 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 202 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 4.5E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 4.5E-5 1/K | ISO 11359-2 | 23°C to 150°C | ||
Entflammbarkeit | UL Recognized, 94V-0 Flame Class Rating: 1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221112- - | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Durchschlagfestigkeit | 23.0 °C | 17 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 17 kV/mm | IEC 60243-1 | in oil, 3.2 mm, |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm | >, IEC 60093 | |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schrumpfung | 23.0 °C | 0.5 % Show Supplier Material materials with Schrumpfung of 0.5 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Electronic Components | |
| Availability | Europe,Americas | |
| Processing methods | Melt Temperature: 370 to 410.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |