Eigenschaften
Allgemein
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 120 MPa Show Supplier Material materials with Biegefestigkeit of 120 MPa | ISO 178 | break, 2 mm/min |
Biegemodul | 23.0 °C | 4.5 GPa Show Supplier Material materials with Biegemodul of 4.5 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 2.5 % Show Supplier Material materials with Dehnung of 2.5 % | ISO 527 | break, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 6 GPa Show Supplier Material materials with Elastizitätsmodul of 6 GPa | ISO 527 | 1 mm/min |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 23 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 23 kJ/m² | ISO 180/1U | unnotched 80*10*4, -30°C |
Zugfestigkeit | 23.0 °C | 80 MPa Show Supplier Material materials with Zugfestigkeit of 80 MPa | ISO 527 | break, 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 120 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 120 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 3E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 3E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Relative temperature index, electrical | 65 °C Show Supplier Material materials with Relative temperature index, electrical of 65 °C | UL 746B | |||
Relative temperature index, mechanical impact | 65 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | |||
Relative temperature index, mechanical strength | 65 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | |||
Vicat-Erweichungstemperatur | 140 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 140 °C | ISO 306 | Rate B/120 | |||
Wärmeformbeständigkeitstemperatur | 120 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 120 °C | ||||
Entflammbarkeit | UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 <br> UV-light, water exposure/immersion: F1- UL 746C <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=228545- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=237020- - | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Kriechstromfestigkeit | 23.0 °C | 250 V Show Supplier Material materials with Kriechstromfestigkeit of 250 V | IEC 60112 | |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzvolumenflussrate | 2 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 2 cm³/10min | ISO 1133 | MVR at 280°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.2 % Show Supplier Material materials with Schrumpfung of 0.2 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Wire & cable | |
| Availability | Europe,Asia | |
| Processing methods | Drying Temperature: 110 to 120.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |