Eigenschaften
Allgemein
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 85 MPa Show Supplier Material materials with Biegefestigkeit of 85 MPa | ISO 178 | yield, 2 mm/min |
Biegemodul | 23.0 °C | 2.2 GPa Show Supplier Material materials with Biegemodul of 2.2 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 30 % Show Supplier Material materials with Dehnung of 30 % | ISO 527 | break, 50 mm/min |
Elastizitätsmodul | 23.0 °C | 0.8 GPa Show Supplier Material materials with Elastizitätsmodul of 0.8 GPa | ASTM D 638 | 50 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 202 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 202 J/m | ASTM D 256 | notched, 23°C |
Instrumented Impact, at Peak | 23.0 °C | 40 J Show Supplier Material materials with Instrumented Impact, at Peak of 40 J | ASTM D 3763 | 23°C |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, -30°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 10 kJ/m² | ISO 180/1A | notched 80*10*4, -30°C |
Zugfestigkeit | 23.0 °C | 55 MPa Show Supplier Material materials with Zugfestigkeit of 55 MPa | ISO 527 | break, 50 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 185 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 185 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |||
Heat deflection temperature, 1.80 MPa | 148 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 148 °C | ASTM D 648 | 3.2mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 8E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 8E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Relative temperature index, electrical | 65 °C Show Supplier Material materials with Relative temperature index, electrical of 65 °C | UL 746B | |||
Relative temperature index, mechanical impact | 65 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | |||
Relative temperature index, mechanical strength | 65 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | |||
Vicat-Erweichungstemperatur | 190 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 190 °C | ISO 306 | Rate B/50 | |||
Wärmeformbeständigkeitstemperatur | 148 - 185 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 148 - 185 °C | ||||
Wärmeleitfähigkeit | 23.0 °C | 0.25 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 0.25 W/(m·K) | ASTM C177 | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 8E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 8E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Entflammbarkeit | UL Recognized, 94HB Flame Class Rating: 1.2mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=102330645- - | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 45 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 45 g/10min | ASTM D 1238 | 280°C/5.0 kgf | |
Schmelzvolumenflussrate | 5 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 5 cm³/10min | ISO 1133 | MVR at 280°C/1.2 kg | |
Schrumpfung | 23.0 °C | 1.3 % Show Supplier Material materials with Schrumpfung of 1.3 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 1 % Show Supplier Material materials with Schrumpfung, diagonal of 1 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Sensor, Wheel Cover, Transmission/Transfer Comp, Traction Motor, Auto Electrical, Electronic Components, Heavy Vehicles | |
| Availability | Asia,Americas | |
| Processing methods | Drying Time: 3 to 4.0hrs | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |