Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.46 g/cm³ Show Supplier Material materials with Dichte of 1.46 g/cm³ | ISO 1183 |
Relative Dichte | 23.0 °C | 1.46 [-] Show Supplier Material materials with Relative Dichte of 1.46 [-] | ASTM D 792 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 125 MPa Show Supplier Material materials with Biegefestigkeit of 125 MPa | ISO 178 | break, 2 mm/min |
Biegemodul | 23.0 °C | 6.3 GPa Show Supplier Material materials with Biegemodul of 6.3 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 2 % Show Supplier Material materials with Dehnung of 2 % | ISO 527 | yield, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 7.4 GPa Show Supplier Material materials with Elastizitätsmodul of 7.4 GPa | ISO 527 | 1 mm/min |
Flexural strain | 23.0 °C | 3 % Show Supplier Material materials with Flexural strain of 3 % | ISO 178 | break, 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 142 MPa Show Supplier Material materials with Hardness, Ball Indentation of 142 MPa | ISO 2039-1 | H358/30 |
Hardness, Rockwell R | 23.0 °C | 120 [-] Show Supplier Material materials with Hardness, Rockwell R of 120 [-] | ISO 2039-2 |
Impact strength, Izod notched, ASTM | 23.0 °C | 45 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 45 J/m | ASTM D 256 | notched, -30°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 330 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 330 J/m | ASTM D 4812 | 23°C |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 5 kJ/m² | ISO 179/2C | -30°C |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 20 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 20 kJ/m² | ISO 179/2C | -30°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 5 kJ/m² | ISO 180/1A | 80*10*4, 0°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 22 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 22 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 75 MPa Show Supplier Material materials with Zugfestigkeit of 75 MPa | ISO 527 | yield, 5 mm/min |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Ball Pressure Test | nan | IEC 60695-10-2 | 125°C +/- 2°C | |||
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | ||||
Glow Wire Ignition Temperature | 750 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 750 °C | IEC 60695-2-13 | 0.8 mm | |||
Heat deflection temperature, 0.45 MPa | 215 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 215 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 180 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 180 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 3.1E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 3.1E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Relative temperature index, electrical | 130 °C Show Supplier Material materials with Relative temperature index, electrical of 130 °C | UL 746B | |||
Relative temperature index, mechanical impact | 75 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 75 °C | UL 746B | |||
Relative temperature index, mechanical strength | 130 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | |||
Vicat-Erweichungstemperatur | 200 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 200 °C | ISO 306 | Rate B/120 | |||
Wärmeformbeständigkeitstemperatur | 180 - 215 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 180 - 215 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.65E-4 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.65E-4 1/K | ISO 11359-2 | 23°C to 150°C | ||
Entflammbarkeit | UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 <br> UL Recognized, 94-5VA Flame Class Rating: ≥2mm UL 94 <br> Glow Wire Ignitability Temperature, 1.5 mm: 750°C IEC 60695-2-13 <br> Glow Wire Flammability Index, 1.5 mm: 850°C IEC 60695-2-12 <br> Glow Wire Flammability Index, 0.8 mm: 960°C IEC 60695-2-12 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=100700420- - |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 3.3 [-] Show Supplier Material materials with Dielektrizitätskonstante, 1 MHz of 3.3 [-] | IEC 60250 |
Dissipation factor, 1MHz | 23.0 °C | 0.01 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 0.01 [-] | IEC 60250 |
Durchschlagfestigkeit | 23.0 °C | 38 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 38 kV/mm | IEC 60243-1 | in oil, 0.8 mm |
High Amp Arc Ignition | 23.0 °C | 0.8 mm Show Supplier Material materials with High Amp Arc Ignition of 0.8 mm | ≥, UL 746A | PLC 0 |
Hot-Wire Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm | ≥, UL 746A | PLC 0 |
Kriechstromfestigkeit | 23.0 °C | 1 V Show Supplier Material materials with Kriechstromfestigkeit of 1 V | UL 746A | (UL) {PLC} |
Sheet resistivity, ROA | 23.0 °C | 1.00E+15 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+15 Ω | >, IEC 60093 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 60093 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt viscosity | 23.0 °C | 145 Pa·s Show Supplier Material materials with Melt viscosity of 145 Pa·s | ISO 11443 | 260°C, 1500 sec-1 |
Schmelzmassenflussrate | 15 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 15 g/10min | ISO 1133 | 250°C/5.0 kg | |
Schmelzvolumenflussrate | 45 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 45 cm³/10min | ISO 1133 | MVR at 265°C/5.0 kg |
Technological properties
Property | ||
---|---|---|
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 110 to 120.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |