Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.29 g/cm³ Show Supplier Material materials with Dichte of 1.29 g/cm³ | ISO 1183 |
Relative Dichte | 23.0 °C | 1.29 [-] Show Supplier Material materials with Relative Dichte of 1.29 [-] | ASTM D 792 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 96 MPa Show Supplier Material materials with Biegefestigkeit of 96 MPa | ISO 178 | yield, 2 mm/min |
Biegemodul | 23.0 °C | 2.3 GPa Show Supplier Material materials with Biegemodul of 2.3 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 92 % Show Supplier Material materials with Dehnung of 92 % | ISO 527 | break, 50 mm/min |
Elastizitätsmodul | 23.0 °C | 2.3 GPa Show Supplier Material materials with Elastizitätsmodul of 2.3 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 123 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 123 J/m | ASTM D 256 | notched, -30°C |
Instrumented Impact, Total Energy | 23.0 °C | 74 J Show Supplier Material materials with Instrumented Impact, Total Energy of 74 J | ASTM D 3763 | 23°C |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 27 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 27 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 13 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 13 kJ/m² | ISO 180/1A | notched 80*10*4, -30°C |
Zugfestigkeit | 23.0 °C | 65 MPa Show Supplier Material materials with Zugfestigkeit of 65 MPa | ISO 527 | yield, 50 mm/min |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Ball pressure temperature | 125 °C Show Supplier Material materials with Ball pressure temperature of 125 °C | IEC 60695-10-2 | approximate maximum | |||
Heat deflection temperature, 1.80 MPa | 131 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 131 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 6E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 6E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Vicat-Erweichungstemperatur | 154 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 154 °C | ISO 306 | Rate B/120 | |||
Wärmeformbeständigkeitstemperatur | 131 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 131 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 6.3E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 6.3E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Entflammbarkeit | OSU peak heat release rate (5 minute test): <65kW/m² FAR 25.853 <br> NBS Smoke Density, Flaming, Dmax: <40- ASTM E 662 <br> Vertical Burn a (60s) passes at: <15sec FAR 25.853 <br> Vertical Burn b (12s) passes at: <15sec FAR 25.853 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 10 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 10 g/10min | ASTM D 1238 | 300°C/1.2 kgf | |
Schmelzvolumenflussrate | 44 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 44 cm³/10min | ISO 1133 | MVR at 300°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.6 % Show Supplier Material materials with Schrumpfung of 0.6 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Aircraft Seating | |
Availability | Americas | |
Processing methods | Screw Speed: 40 to 70.0rpm | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |