Allgemein
Property | Value | Comment |
---|---|---|
Coefficient of friction | 0.67 - 0.87 [-] Show Supplier Material materials with Coefficient of friction of 0.67 - 0.87 [-] | |
Coefficient of friction, kinetic | 0.67 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.67 [-] | ASTM D 3702 Modified: Manual |
Coefficient of friction, static | 0.87 [-] Show Supplier Material materials with Coefficient of friction, static of 0.87 [-] | ASTM D 3702 Modified: Manual |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 235 MPa Show Supplier Material materials with Biegefestigkeit of 235 MPa | ISO 178 | break, 2 mm/min |
Biegemodul | 23.0 °C | 8.6 GPa Show Supplier Material materials with Biegemodul of 8.6 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 2.9 % Show Supplier Material materials with Dehnung of 2.9 % | ISO 527 | yield, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 10.2 GPa Show Supplier Material materials with Elastizitätsmodul of 10.2 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 95 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 95 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 1000 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 1000 J/m | ASTM D 4812 | 23°C |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 11 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 11 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 12 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 12 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 75 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 75 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 155 MPa Show Supplier Material materials with Zugfestigkeit of 155 MPa | ISO 527 | break, 5 mm/min |
Thermisch
Property | Temperature | Value | Comment |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 215 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 215 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 200 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 200 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 2.4E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 2.4E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Vicat-Erweichungstemperatur | 210 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 210 °C | ISO 306 | Rate B/50 | |
Wärmeformbeständigkeitstemperatur | 200 - 215 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 200 - 215 °C | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 9.6E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 9.6E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Wiring Devices | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 80°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |