Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.19 g/cm³ Show Supplier Material materials with Dichte of 1.19 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.09 % Show Supplier Material materials with Moisture absorption of 0.09 % | ISO 62 | (23°C / 50% RH) |
Relative Dichte | 23.0 °C | 1.19 [-] Show Supplier Material materials with Relative Dichte of 1.19 [-] | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.13 % Show Supplier Material materials with Wasserabsorption of 0.13 % | ISO 62-1 | (23°C/saturated) |
Mechanisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Biegefestigkeit | 23.0 °C | 91 MPa Show Supplier Material materials with Biegefestigkeit of 91 MPa | ISO 178 | yield, 2 mm/min | ||
Biegemodul | 23.0 °C | 2.2 GPa Show Supplier Material materials with Biegemodul of 2.2 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 5.6 % Show Supplier Material materials with Dehnung of 5.6 % | ISO 527 | yield, 50 mm/min | ||
Elastizitätsmodul | 23.0 °C | 2.3 GPa Show Supplier Material materials with Elastizitätsmodul of 2.3 GPa | ISO 527 | 1 mm/min | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 795 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 795 J/m | ASTM D 256 | notched, -30°C | ||
Instrumented Impact, Total Energy | 23.0 °C | 82 J Show Supplier Material materials with Instrumented Impact, Total Energy of 82 J | ASTM D 3763 | 23°C | ||
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 70 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 70 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, 23°C | ||
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 55 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 55 kJ/m² | ISO 180/1A | notched 80*10*3, -30°C | ||
Zugfestigkeit | 23.0 °C | 57 MPa Show Supplier Material materials with Zugfestigkeit of 57 MPa | ISO 527 | yield, 50 mm/min | ||
Schlagzähigkeit, Charpy ungekerbt | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm, -30°C | ||||
Schlagzähigkeit, Izod ungekerbt | ISO 180/1U | 80*10*3, 23°C |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Ball Pressure Test | PASS | IEC 60695-10-2 | 125°C +/- 2°C | |||
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | ||||
Glow Wire Ignition Temperature | 825 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 825 °C | IEC 60695-2-13 | 3.0 mm | |||
Heat deflection temperature, 1.80 MPa | 119 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 119 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 7.15E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 7.15E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Vicat-Erweichungstemperatur | 143 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 143 °C | ISO 306 | Rate B/120 | |||
Wärmeformbeständigkeitstemperatur | 119 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 119 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 7.93E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 7.93E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Entflammbarkeit | UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 <br> Glow Wire Ignitability Temperature, 1.5 mm: 825°C IEC 60695-2-13 <br> Glow Wire Flammability Index, 1.5 mm: 850°C IEC 60695-2-12 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=512742- - |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
High Amp Arc Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm | ≥, UL 746A | PLC 1 |
Hot-Wire Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm | ≥, UL 746A | PLC 3 |
Kriechstromfestigkeit | 23.0 °C | 3 V Show Supplier Material materials with Kriechstromfestigkeit of 3 V | UL 746A | (UL) {PLC} |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 10 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 10 g/10min | ASTM D 1238 | 300°C/1.2 kgf | |
Schmelzvolumenflussrate | 9 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 9 cm³/10min | ISO 1133 | MVR at 220°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.4 % Show Supplier Material materials with Schrumpfung of 0.4 % | SABIC method | on tensile bar |
Schrumpfung, diagonal | 23.0 °C | 0.4 % Show Supplier Material materials with Schrumpfung, diagonal of 0.4 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Medical Device, Personal Computing, Enclosures, Heavy Vehicles, Document Handling, Console, Audio | |
Availability | Europe,Asia,Americas | |
Processing methods | Front - Zone 3 Temperature: 295 to 315.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |