Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.69 g/cm³ Show Supplier Material materials with Dichte of 1.69 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.04 % Show Supplier Material materials with Moisture absorption of 0.04 % | ISO 62 | (23°C / 50% RH) |
Relative Dichte | 23.0 °C | 1.69 [-] Show Supplier Material materials with Relative Dichte of 1.69 [-] | ASTM D 792 | |
Wasserabsorption | 23.0 °C | 0.1 % Show Supplier Material materials with Wasserabsorption of 0.1 % | ISO 62-1 | (23°C/saturated) |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 172 MPa Show Supplier Material materials with Biegefestigkeit of 172 MPa | ISO 178 | yield, 2 mm/min |
Biegemodul | 23.0 °C | 13.6 GPa Show Supplier Material materials with Biegemodul of 13.6 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 1.4 % Show Supplier Material materials with Dehnung of 1.4 % | ISO 527 | break, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 14.7 GPa Show Supplier Material materials with Elastizitätsmodul of 14.7 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 49 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 49 J/m | ASTM D 256 | notched, -30°C |
Instrumented Impact, Total Energy | 23.0 °C | 12 J Show Supplier Material materials with Instrumented Impact, Total Energy of 12 J | ASTM D 3763 | 23°C |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 4 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 4 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 5 kJ/m² | ISO 180/1A | 80*10*4, -30°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 5 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 121 MPa Show Supplier Material materials with Zugfestigkeit of 121 MPa | ISO 527 | break, 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Ball Pressure Test | Passes | IEC 60695-10-2 | 125°C +/- 2°C | |
Heat deflection temperature, 0.45 MPa | 195 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 195 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 182 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 182 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.6E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.6E-5 1/K | ISO 11359-2 | 23°C to 150°C |
Vicat-Erweichungstemperatur | 195 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 195 °C | ISO 306 | Rate B/120 | |
Wärmeformbeständigkeitstemperatur | 182 - 195 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 182 - 195 °C | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 3.8E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 3.8E-5 1/K | ISO 11359-2 | 23°C to 150°C |
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 2.10E+15 Ω Show Supplier Material materials with Sheet resistivity, ROA of 2.10E+15 Ω | ASTM D 257 |
Volume resistivity | 23.0 °C | 6.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 6.00E+15 Ω·cm | ASTM D 257 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 20 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 20 g/10min | ASTM D 1238 | 337°C/6.6 kgf | |
Schmelzvolumenflussrate | 20 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 20 cm³/10min | ISO 1133 | MVR at 360°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.2 % Show Supplier Material materials with Schrumpfung of 0.2 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.3 % Show Supplier Material materials with Schrumpfung, diagonal of 0.3 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Time: 4 to 6.0hrs | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |