Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.53 g/cm³ Show Supplier Material materials with Dichte of 1.53 g/cm³ | ASTM D 792 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 307 MPa Show Supplier Material materials with Biegefestigkeit of 307 MPa | ISO 178 |
Biegemodul | 23.0 °C | 12 GPa Show Supplier Material materials with Biegemodul of 12 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 2.8 % Show Supplier Material materials with Dehnung of 2.8 % | ISO 527 | break, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 14 GPa Show Supplier Material materials with Elastizitätsmodul of 14 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 162 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 162 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 1400 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 1400 J/m | ASTM D 4812 | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 19 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 19 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 214 MPa Show Supplier Material materials with Zugfestigkeit of 214 MPa | ISO 527 | break, 5 mm/min |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 247 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 247 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Relative temperature index, electrical | 130 °C Show Supplier Material materials with Relative temperature index, electrical of 130 °C | UL 746B | |
Relative temperature index, mechanical impact | 105 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | |
Relative temperature index, mechanical strength | 115 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 115 °C | UL 746B | |
Wärmeformbeständigkeitstemperatur | 247 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 247 °C | ||
Entflammbarkeit | UL Recognized, 94V-0 Flame Class Rating: ≥1.7mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103093596- - |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
High Amp Arc Ignition | 23.0 °C | 3 mm Show Supplier Material materials with High Amp Arc Ignition of 3 mm | ≥, UL 746A | PLC 0 |
High Volt Arc Track Rate | 23.0 °C | 1 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 1 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 3 mm Show Supplier Material materials with Hot-Wire Ignition of 3 mm | ≥, UL 746A | PLC 0 |
Kriechstromfestigkeit | 23.0 °C | 3 V Show Supplier Material materials with Kriechstromfestigkeit of 3 V | UL 746A | (UL) {PLC} |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schrumpfung | 23.0 °C | 0.3 % Show Supplier Material materials with Schrumpfung of 0.3 % | ASTM D 955 | 24 hrs |
Technological properties
Property | ||
---|---|---|
Application areas | Lawn/Garden | |
Availability | Asia,Americas | |
Processing methods | Screw Speed: 30 to 60.0rpm | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |