Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Relative Dichte | 23.0 °C | 1.61 [-] Show Supplier Material materials with Relative Dichte of 1.61 [-] | ASTM D 792 | |
Sauerstoffindex | 23.0 °C | 48 % Show Supplier Material materials with Sauerstoffindex of 48 % | |
Wasserabsorption | 23.0 °C | 0.8 % Show Supplier Material materials with Wasserabsorption of 0.8 % | ISO 62-1 | (23°C/saturated) |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 240 MPa Show Supplier Material materials with Biegefestigkeit of 240 MPa | ISO 178 | break, 2 mm/min |
Biegemodul | 23.0 °C | 10 GPa Show Supplier Material materials with Biegemodul of 10 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 2 % Show Supplier Material materials with Dehnung of 2 % | ISO 527 | break, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 11.5 GPa Show Supplier Material materials with Elastizitätsmodul of 11.5 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 112 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 112 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 427 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 427 J/m | ASTM D 4812 | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 112 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 112 kJ/m² | ASTM D 256 | notched, 23°C |
Zugfestigkeit | 23.0 °C | 180 MPa Show Supplier Material materials with Zugfestigkeit of 180 MPa | ISO 527 | break, 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 215 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 215 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |||
Heat deflection temperature, 1.80 MPa | 210 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 210 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.5E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.5E-5 1/K | ISO 11359-2 | 23°C to 150°C | ||
Relative temperature index, electrical | 105 °C Show Supplier Material materials with Relative temperature index, electrical of 105 °C | UL 746B | |||
Relative temperature index, mechanical impact | 105 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | |||
Relative temperature index, mechanical strength | 105 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C | UL 746B | |||
Vicat-Erweichungstemperatur | 230 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 230 °C | ISO 306 | Rate A/50 | |||
Wärmeformbeständigkeitstemperatur | 210 - 215 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 210 - 215 °C | ||||
Entflammbarkeit | UL Recognized, 94-5VA Flame Class Rating: ≥1.5mm UL 94 <br> Glow Wire Flammability Index 960°C, passes at: 3.2mm IEC 60695-2-12 <br> Glow Wire Flammability Index 960°C, passes at: 3.2mm IEC 60695-2-12 <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.25mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221104- - | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dissipation factor, 1kHz | 23.0 °C | 2E-3 [-] Show Supplier Material materials with Dissipation factor, 1kHz of 2E-3 [-] | IEC 60250 |
Durchschlagfestigkeit | 23.0 °C | 16 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 16 kV/mm | IEC 60243-1 | in oil, 3.2 mm, |
High Amp Arc Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm | ≥, UL 746A | PLC 4 |
High Volt Arc Track Rate | 23.0 °C | 4 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 4 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm | ≥, UL 746A | PLC 0 |
Kriechstromfestigkeit | 23.0 °C | 4 V Show Supplier Material materials with Kriechstromfestigkeit of 4 V | UL 746A | (UL) {PLC} |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 60093 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schrumpfung | 23.0 °C | 0.1 % Show Supplier Material materials with Schrumpfung of 0.1 % | SABIC method | on tensile bar |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Electronic Components, Document Handling, Data Transfer, Watch/Jewelry | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Hopper Temperature: 80 to 100.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |