Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.42 g/cm³ Show Supplier Material materials with Dichte of 1.42 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.55 % Show Supplier Material materials with Moisture absorption of 0.55 % | ISO 62 | (23°C / 50% RH) |
Sauerstoffindex | 23.0 °C | 50 % Show Supplier Material materials with Sauerstoffindex of 50 % | |
Wasserabsorption | 23.0 °C | 1 % Show Supplier Material materials with Wasserabsorption of 1 % | ISO 62-1 | (23°C/saturated) |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 228 MPa Show Supplier Material materials with Biegefestigkeit of 228 MPa | ISO 178 | yield, 2 mm/min |
Biegemodul | 23.0 °C | 6.5 GPa Show Supplier Material materials with Biegemodul of 6.5 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 2 % Show Supplier Material materials with Dehnung of 2 % | ISO 527 | break, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 6.9 GPa Show Supplier Material materials with Elastizitätsmodul of 6.9 GPa | ISO 527 | 1 mm/min |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 65 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 65 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Zugfestigkeit | 23.0 °C | 131 MPa Show Supplier Material materials with Zugfestigkeit of 131 MPa | ISO 527 | break, 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Ball Pressure Test | nan | IEC 60695-10-2 | 125°C +/- 2°C | |||
Heat deflection temperature, 1.80 MPa | 205 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 205 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 2.5E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 2.5E-5 1/K | ISO 11359-2 | 23°C to 150°C | ||
Relative temperature index, electrical | 170 °C Show Supplier Material materials with Relative temperature index, electrical of 170 °C | UL 746B | |||
Relative temperature index, mechanical impact | 170 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 170 °C | UL 746B | |||
Relative temperature index, mechanical strength | 170 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 170 °C | UL 746B | |||
Vicat-Erweichungstemperatur | 218 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 218 °C | ISO 306 | Rate B/120 | |||
Wärmeformbeständigkeitstemperatur | 205 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 205 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 6E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 6E-5 1/K | ISO 11359-2 | 23°C to 150°C | ||
Entflammbarkeit | UL Recognized, 94-5VA Flame Class Rating: ≥1.9mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.41mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221093- - | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Durchschlagfestigkeit | 23.0 °C | 26.3 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 26.3 kV/mm | ASTM D 149 | in oil, 1.6 mm |
High Amp Arc Ignition | 23.0 °C | 3 mm Show Supplier Material materials with High Amp Arc Ignition of 3 mm | ≥, UL 746A | PLC 4 |
High Volt Arc Track Rate | 23.0 °C | 2 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 2 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 3 mm Show Supplier Material materials with Hot-Wire Ignition of 3 mm | ≥, UL 746A | PLC 1 |
Kriechstromfestigkeit | 23.0 °C | 4 V Show Supplier Material materials with Kriechstromfestigkeit of 4 V | UL 746A | (UL) {PLC} |
Verlustfaktor | 23.0 °C | 4.9E-3 [-] Show Supplier Material materials with Verlustfaktor of 4.9E-3 [-] | ASTM D 150 | 2450 MHz |
Volume resistivity | 23.0 °C | 7.00E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 7.00E+16 Ω·cm | ASTM D 257 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzvolumenflussrate | 7 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 7 cm³/10min | ISO 1133 | MVR at 360°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.3 % Show Supplier Material materials with Schrumpfung of 0.3 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Heavy Vehicles | |
| Availability | Europe,Americas | |
| Processing methods | Mold Temperature: 135 to 165.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |